Abstract:During the train operation, the pantograph/catenary system is subjected to an extremely harsh service environment. Relative humidity has a great influence on the current-carrying tribological behaviors of carbon strips. The identification and understanding of the wear mechanism are extremely important in wet and dry conditions. This study was carried out to investigate the humidity effect on the service properties of carbon sample rubbing against copper (Cu) with and without electric current using a home-made wear tester, and the humidity ranging from 10% RH to 80% RH. The results indicate that the sliding wear behavior of the friction interface is drastically affected by the intervention of water vapor and electric current. The coefficient of friction (COF) without current is obviously lower than current-carrying sliding when the humidity is constant. However, the increased humidity led to a decreasing trend. After the current increases to 10 A, all the COF values are closed to each other ultimately. These phenomena mainly result from the formation and destruction of water lubrication film. Furthermore, the tribo-pairs worn surface appears the most sensitive to the current effect under dry conditions. The reverse transfer of Cu and carbon is greater on account of the current agglomeration effect, and the oxidation degree is more severe. The wear mechanisms of carbon are mainly material transfer accompanying with oxidation erosion. However, the wear degradation is weakened under water lubrication and uniform current distribution which improves the conductive quality. This is the coupling effect of humidity environment, current and heat concentration. This experiment provides technical support for the operation of an electric locomotive under an extremely harsh service environment.

Effect of Humidity on the Wear Behavior of Graphene under Current Carrying Conditions

Lubrication Performance of Graphene in the Sliding Electrical Contact Interface

Impacts of environments on nanoscale wear behavior of graphene: Edge passivation vs. substrate pinning

First-Principles Study of the Friction and Wear Resistance of Graphene Sheets

Effect of airborne contaminants on the macroscopic anti-wear performance of chemical vapor deposition graphene

Influence of Humidity on Contact Resistance in Graphene Devices

Wear Evolution of Monolayer Graphene at the Macroscale

Study on the Lubricating Characteristics of Graphene Lubricants

Humidity-dependent lubrication of highly loaded contacts by graphite and a structural transition to turbostratic carbon

Effect of Relative Humidity on the Tribological/conductive Properties of Cu/Cu Rolling Contact Pairs

Effect of Two Graphene Coatings on the Friction and Wear of Sliding Electrical Contact Interface

Lubrication Performance of Hydrogenated Graphene on Diamond-Like Carbon Films Based on Molecular Dynamics Simulation

Lubrication Properties of Graphene under Harsh Working Conditions

The role of relatively humidity in friction and wear behaviors of carbon sliding against copper with electric current

Macroscale, Humidity-Insensitive, and Stable Structural Superlubricity Achieved with Hydrogen-Free Graphene Nanoflakes

Electric Resistance As a Sensitive Measure for Detecting Graphene Wear During Macroscale Tribological Tests

Graphene as a Lubricant Additive for Reducing Friction and Wear in Its Liquid-Based Form

Graphene-Family Lubricant Additives: Recent Developments and Future Perspectives

Graphene-induced reconstruction of the sliding interface assisting the improved lubricity of various tribo-couples

Graphene as a protective coating and superior lubricant for electrical contacts

Structure, superlubricity, applications, and chemical vapor deposition methods of graphene solid lubricants