Research on Selective Laser Sintering Process of Limestone/Polyethersulfone Composites
Guo, Yanling
DOI: https://doi.org/10.1007/s11665-022-06939-6
IF: 2.3
2022-05-10
Journal of Materials Engineering and Performance
Abstract:Owing to its high melting point, limestone powder cannot be directly used to fabricate parts through laser sintering. To address this issue, a polyethersulfone (PES)-based polymer matrix composite material, in which PES serves as a binder between particles of limestone powder, is introduced to prepare composite artificial stone parts using the selective laser sintering technology. Preliminary single-factor experiments were conducted for sintered limestone/PES (LPES) composite parts with different component ratios (R), laser sintering power (P), and powder bed preheating temperature (T) to determine the range of test parameters. Subsequently, using the laser power (x 1 ), scanning speed (x 2 ), scan spacing (x 3 ), and layer thickness (x 4 ) as experimental factors and the impact strength (y 1 ) and dimensional accuracy along X, Y, and Z directions, respectively (y 2 , y 3 , and y 4 ), of impact sintered parts as experimental indices, a four-factor three-level orthogonal experiment was conducted for optimization. The optimal combination of parameters affecting the multiobjective function within the tested range was obtained: laser power (15 W), scanning speed (1800 mm/s), scan spacing (0.1 mm), and layer thickness (0.1 mm). For this optimal combination, the sintered LPES model possesses an impact strength of 170.69 MPa and dimensional accuracies of 98.29% along the X direction, 97.36% along the Y direction, and 92.81% along the Z direction. Compared with a pure PES specimen, the impact strength was improved by 42.89%, and the dimensional accuracy was improved by 0.91% along the X direction, 1.23% along the Y direction, and 3.43% along the Z direction.
materials science, multidisciplinary