Abstract:A novel bio-based benzoxazine resin (phenolphthalein-furfuramine-benzoxazine , PTL-F-BOZ) , used bio-based furfurylamine , phenolphthalein , and paraformaldehyde as raw materials , was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) , nuclear magnetic resonance (H-1 NMR and C-13 NMR) . The curing , thermal and flame retardant properties were analyzed by differential scanning calorimetric (DSC) , thermogravimetric analyzer (TG) , limiting oxygen index (LOI) , vertical burning test, microscale combustion calorimetry (MCC) , cone calorimeter(Cone) and scanning electron microscope (SEM) . The DSC curve of PTL-F-BOZ showed a two-stage curing with two maxima at 224 and 251 degrees C respectively, and had lower curing temperature than that of the traditional fossil-based bisphenol benzoxazine bisphenol A-aniline benzoxazine (bisphenol A-aniline-benzoxazine , BPA-A-BOZ) . The presence of the furan ring in the furfurylamine increased the cross-linking density of polymer, retarded the rearrangement reaction from the phenoxy structure to the phenol structure, and resulted in two curing peaks in the DSC curve of PTL-F-BOZ. Under nitrogen and air atmospheres, the temperatures of 5% mass loss (T-5%) for PPTL-F-BOZ resin were 380 and 370 degrees C , respectively and the residual chars at 800 degrees C were 63. 0% and 10. 5% , respectively. Compared with PBPA-A-BOZ resin, PPTL-F-BOZ resin both possessed higher T-5% and residual char of 800 degrees C. From the DTG curve , the maximum mass loss rates of two decomposition stage (Peak 1 and Peak 2 values) of PPTL-FBOZ resin were 0. 67%/min and 3. 28%/min, which were only 7. 38% and 63. 44% of PBPA-A-BOZ (9. 07%/min and 5. 17%/min) under nitrogen atmosphere , and those were also the same under air atmosphere. LOI of PPTL-F-BOZ resin was 36. 2%, which was higher than that of PBPA-A-BOZ resin. Meanwhile, in the UL-94 test, PPTL-F-BOZ resin extinguished quickly and released less smoke during combustion process, and the original morphology was kept well and a stable carbon layer was formed after burning. Its first ignition time(t(1)) and second ignition time(t(2)) were 1. 4 and 8. 5 s , respectively , far smaller than the maximum permissible values of 10 s, and a UL94 V-0 rating was also achieved. Hence, PPTL-F-BOZ resin showed excellent thermal and flame retardant properties.

Polypyrrole inter-layered low temperature curing benzoxazine matrices with enhanced thermal and dielectric properties

Synthesis and Properties of a Novel Bio‐based Benzoxazine Resin with Excellent Low‐temperature Curing Ability

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis, Curing, and Thermal Stability of Low-Temperature-Cured Benzoxazine Resins Based on Natural Renewable Resources

Synthesis of Aromatic Diamine-Based Benzoxazines and Effect of Their Backbone Structure on Thermal and Flammability Properties of Polymers

Synthesis and Properties of a Novel Bio-based Benzoxazine

Highly Thermal Conductive Benzoxazine‐epoxy Interpenetrating Polymer Networks Containing Liquid Crystalline Structures

Synthesis, characterization, and thermal properties of benzoxazine monomers containing allyl groups

Probing the copolymerization of alkynyl and cyano groups using monocyclic benzoxazine as model compound

Thermal, mechanical and dielectric property enhancement of benzoxazine-containing phthalonitrile resin: The effect of functional oligomeric polyphenyl ether

Synthesis and characterization of cardo-tetrafunctional hydrophobic polybenzoxazine composites for low-k application

Greatly Enhanced Thermo-Oxidative Stability Of Polybenzoxazine Thermoset By Incorporation Of M-Carborane

Curing reaction mechanism and heat resistance properties of hexa‐(4‐carboxyl‐phenoxy)‐cyclotriphosphazene/bisphenol A aniline benzoxazine blends

Preparation of biphenyl-containing polybenzoxazines with low dielectric constants and high thermal stability

Studies on catalyst assisted low-temperature curing of benzoxazines

Sustainable synthesis of a novel bio-based low temperature curable benzoxazine monomer from quercetin: Synthesis, curing reaction and thermal properties

Melamine as cross‐linking agent for mono‐cyclic benzoxazine with aldehyde groups: higher crosslinking density and thermal properties

Preparation, Curing Properties, and Phase Morphology of Epoxy-Novolac Resin/multiepoxy-Terminated Low-Molecular-weight Poly(phenylene Oxide) Blend

Properties and Curing Kinetics of a Processable Binary Benzoxazine Blend

Thermosetting benzoxazoles with endo-alkynyl groups: excellent thermal stability and low dielectric loss

Curing reaction and properties of a kind of fluorinated phthalonitrile containing benzoxazine