Abstract:A novel bio-based benzoxazine resin (phenolphthalein-furfuramine-benzoxazine , PTL-F-BOZ) , used bio-based furfurylamine , phenolphthalein , and paraformaldehyde as raw materials , was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) , nuclear magnetic resonance (H-1 NMR and C-13 NMR) . The curing , thermal and flame retardant properties were analyzed by differential scanning calorimetric (DSC) , thermogravimetric analyzer (TG) , limiting oxygen index (LOI) , vertical burning test, microscale combustion calorimetry (MCC) , cone calorimeter(Cone) and scanning electron microscope (SEM) . The DSC curve of PTL-F-BOZ showed a two-stage curing with two maxima at 224 and 251 degrees C respectively, and had lower curing temperature than that of the traditional fossil-based bisphenol benzoxazine bisphenol A-aniline benzoxazine (bisphenol A-aniline-benzoxazine , BPA-A-BOZ) . The presence of the furan ring in the furfurylamine increased the cross-linking density of polymer, retarded the rearrangement reaction from the phenoxy structure to the phenol structure, and resulted in two curing peaks in the DSC curve of PTL-F-BOZ. Under nitrogen and air atmospheres, the temperatures of 5% mass loss (T-5%) for PPTL-F-BOZ resin were 380 and 370 degrees C , respectively and the residual chars at 800 degrees C were 63. 0% and 10. 5% , respectively. Compared with PBPA-A-BOZ resin, PPTL-F-BOZ resin both possessed higher T-5% and residual char of 800 degrees C. From the DTG curve , the maximum mass loss rates of two decomposition stage (Peak 1 and Peak 2 values) of PPTL-FBOZ resin were 0. 67%/min and 3. 28%/min, which were only 7. 38% and 63. 44% of PBPA-A-BOZ (9. 07%/min and 5. 17%/min) under nitrogen atmosphere , and those were also the same under air atmosphere. LOI of PPTL-F-BOZ resin was 36. 2%, which was higher than that of PBPA-A-BOZ resin. Meanwhile, in the UL-94 test, PPTL-F-BOZ resin extinguished quickly and released less smoke during combustion process, and the original morphology was kept well and a stable carbon layer was formed after burning. Its first ignition time(t(1)) and second ignition time(t(2)) were 1. 4 and 8. 5 s , respectively , far smaller than the maximum permissible values of 10 s, and a UL94 V-0 rating was also achieved. Hence, PPTL-F-BOZ resin showed excellent thermal and flame retardant properties.

Curing reaction and properties of a kind of fluorinated phthalonitrile containing benzoxazine

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis, Curing, and Thermal Stability of Low-Temperature-Cured Benzoxazine Resins Based on Natural Renewable Resources

Synthesis and Properties of a Novel Bio‐based Benzoxazine Resin with Excellent Low‐temperature Curing Ability

Synthesis and Properties of a Novel Bio-based Benzoxazine

Curing, Thermal Stability and Composite Properties for Blends of the Novel Bismaleimide and Cyanate Containing Naphthalene

Cure of Neat Resins and Properties of Composites for Interpenetrating Polymer Networks from the Novel Bismaleimide and Cyanate Containing Naphthalene

Synthesis of Aromatic Diamine-Based Benzoxazines and Effect of Their Backbone Structure on Thermal and Flammability Properties of Polymers

Modification on phthalonitrile containing benzoxazine with cyaniding diamine-type benzoxazine: Curing reaction and properties of their glass fiber-reinforced composites

Synthesis, characterization and self-promoted cure behaviors of a new phthalonitrile derivative 4-(4-(3, 5-diaminobenzoyl) phenoxy) phthalonitrile

Modification on phthalonitrile containing benzoxazine with hydroxy-terminated polyarylene ether nitrile: Curing reaction and thermomechanical properties

Multiple catalytic polymerization of phthalonitrile resin bearing benzoxazine moiety: Greatly reduced curing temperature

Effect of ortho‐diallyl bisphenol A on the processability of phthalonitrile‐based resin and their fiber‐reinforced laminates

Promoting effect of methyne/methylene moiety of bisphenol E/F on phthalonitrile resin curing: Expanding the structural design route of phthalonitrile resin

Convenient synthesis of phthalonitrile‐containing mono‐benzoxazines with exceptional thermal stability and improved curing activity

A Fluorine-Containing Main-Chain Benzoxazine/Epoxy Co-Curing System with Low Dielectric Constants and High Thermal Stability

Thermal, mechanical and dielectric property enhancement of benzoxazine-containing phthalonitrile resin: The effect of functional oligomeric polyphenyl ether

Branched Fluorine/Adamantane Interfacial Compatibilizer for PBO Fibers/Cyanate Ester Wave-Transparent Laminated Composites

Preparation and properties of high-temperature resistant bisphthalonitrile resins containing trifluoromethyl groups reinforced by poly (aryl ether nitrile) capped by phthalonitrile and composites

Synthesis and characterization of cyano-terminated bisphenol AF-type polyarylene ether nitrile

Thermal Stability of Allyl-Functional Phthalonitriles-Containing Benzoxazine/Bismaleimide Copolymers and Their Improved Mechanical Properties