Abstract:A novel bio-based benzoxazine resin (phenolphthalein-furfuramine-benzoxazine , PTL-F-BOZ) , used bio-based furfurylamine , phenolphthalein , and paraformaldehyde as raw materials , was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) , nuclear magnetic resonance (H-1 NMR and C-13 NMR) . The curing , thermal and flame retardant properties were analyzed by differential scanning calorimetric (DSC) , thermogravimetric analyzer (TG) , limiting oxygen index (LOI) , vertical burning test, microscale combustion calorimetry (MCC) , cone calorimeter(Cone) and scanning electron microscope (SEM) . The DSC curve of PTL-F-BOZ showed a two-stage curing with two maxima at 224 and 251 degrees C respectively, and had lower curing temperature than that of the traditional fossil-based bisphenol benzoxazine bisphenol A-aniline benzoxazine (bisphenol A-aniline-benzoxazine , BPA-A-BOZ) . The presence of the furan ring in the furfurylamine increased the cross-linking density of polymer, retarded the rearrangement reaction from the phenoxy structure to the phenol structure, and resulted in two curing peaks in the DSC curve of PTL-F-BOZ. Under nitrogen and air atmospheres, the temperatures of 5% mass loss (T-5%) for PPTL-F-BOZ resin were 380 and 370 degrees C , respectively and the residual chars at 800 degrees C were 63. 0% and 10. 5% , respectively. Compared with PBPA-A-BOZ resin, PPTL-F-BOZ resin both possessed higher T-5% and residual char of 800 degrees C. From the DTG curve , the maximum mass loss rates of two decomposition stage (Peak 1 and Peak 2 values) of PPTL-FBOZ resin were 0. 67%/min and 3. 28%/min, which were only 7. 38% and 63. 44% of PBPA-A-BOZ (9. 07%/min and 5. 17%/min) under nitrogen atmosphere , and those were also the same under air atmosphere. LOI of PPTL-F-BOZ resin was 36. 2%, which was higher than that of PBPA-A-BOZ resin. Meanwhile, in the UL-94 test, PPTL-F-BOZ resin extinguished quickly and released less smoke during combustion process, and the original morphology was kept well and a stable carbon layer was formed after burning. Its first ignition time(t(1)) and second ignition time(t(2)) were 1. 4 and 8. 5 s , respectively , far smaller than the maximum permissible values of 10 s, and a UL94 V-0 rating was also achieved. Hence, PPTL-F-BOZ resin showed excellent thermal and flame retardant properties.

Sustainable synthesis of a novel bio-based low temperature curable benzoxazine monomer from quercetin: Synthesis, curing reaction and thermal properties

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis, Curing, and Thermal Stability of Low-Temperature-Cured Benzoxazine Resins Based on Natural Renewable Resources

Synthesis and Properties of a Novel Bio‐based Benzoxazine Resin with Excellent Low‐temperature Curing Ability

Synthesis and Properties of a Novel Bio-based Benzoxazine

Bio-based phthalonitrile resin derived from quercetin as a sustainable molecular scaffold: Synthesis, curing reaction and comparison with petroleum-based counterparts

Synthesis, polymerization and thermal properties of bio‐based benzoxazine resins containing imide or amide functionality

Synthesis and characterization of novel bio-based benzoxazines from eugenol

Synthesis, characterization, and thermal properties of benzoxazine monomers containing allyl groups

Film-forming Characteristics and Thermal Stability of Low Viscosity Benzoxazines Derived from Melamine

Synthesis, Polymerization Kinetics and Thermal Properties of Benzoxazine Resin Containing ortho-Maleimide Functionality

Thermosetting benzoxazoles with endo-alkynyl groups: excellent thermal stability and low dielectric loss

Synthesis and Copolymerization of Fully Biobased Benzoxazines from Renewable Resources

Synthesis of Daidzein and Thiophene Containing Benzoxazine Resin and Its Thermoset and Carbon Material

Sustainable Preparation of Bio-Based Polybenzoxazine Resins from Amino Acid and Their Application in CO2 Adsorption

A Bio-Based Polybenzoxazine Derived from Diphenolic Acid with Intrinsic Flame Retardancy, High Glass Transition Temperature and Dielectric Properties.

Quercetin allylation and thiol–ene click photopolymerization to produce biobased polymer thermosets with robust thermomechanical properties

A low cure thermo active polymerization of chalcone based benzoxazine and cross linkable olefin blends

Synthesis of Branched Benzoxazine Monomers with High Molecular Mass, Wide Processing Window, and Properties of Corresponding Polybenzoxazines

Development of Low-Viscosity and High-Performance Biobased Monobenzoxazine from Tyrosol and Furfurylamine

Optimizing mechanical performance in 3D printing through a benzoxazine monomer blend photosensitive resin formulation