Abstract:A novel bio-based benzoxazine resin (phenolphthalein-furfuramine-benzoxazine , PTL-F-BOZ) , used bio-based furfurylamine , phenolphthalein , and paraformaldehyde as raw materials , was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) , nuclear magnetic resonance (H-1 NMR and C-13 NMR) . The curing , thermal and flame retardant properties were analyzed by differential scanning calorimetric (DSC) , thermogravimetric analyzer (TG) , limiting oxygen index (LOI) , vertical burning test, microscale combustion calorimetry (MCC) , cone calorimeter(Cone) and scanning electron microscope (SEM) . The DSC curve of PTL-F-BOZ showed a two-stage curing with two maxima at 224 and 251 degrees C respectively, and had lower curing temperature than that of the traditional fossil-based bisphenol benzoxazine bisphenol A-aniline benzoxazine (bisphenol A-aniline-benzoxazine , BPA-A-BOZ) . The presence of the furan ring in the furfurylamine increased the cross-linking density of polymer, retarded the rearrangement reaction from the phenoxy structure to the phenol structure, and resulted in two curing peaks in the DSC curve of PTL-F-BOZ. Under nitrogen and air atmospheres, the temperatures of 5% mass loss (T-5%) for PPTL-F-BOZ resin were 380 and 370 degrees C , respectively and the residual chars at 800 degrees C were 63. 0% and 10. 5% , respectively. Compared with PBPA-A-BOZ resin, PPTL-F-BOZ resin both possessed higher T-5% and residual char of 800 degrees C. From the DTG curve , the maximum mass loss rates of two decomposition stage (Peak 1 and Peak 2 values) of PPTL-FBOZ resin were 0. 67%/min and 3. 28%/min, which were only 7. 38% and 63. 44% of PBPA-A-BOZ (9. 07%/min and 5. 17%/min) under nitrogen atmosphere , and those were also the same under air atmosphere. LOI of PPTL-F-BOZ resin was 36. 2%, which was higher than that of PBPA-A-BOZ resin. Meanwhile, in the UL-94 test, PPTL-F-BOZ resin extinguished quickly and released less smoke during combustion process, and the original morphology was kept well and a stable carbon layer was formed after burning. Its first ignition time(t(1)) and second ignition time(t(2)) were 1. 4 and 8. 5 s , respectively , far smaller than the maximum permissible values of 10 s, and a UL94 V-0 rating was also achieved. Hence, PPTL-F-BOZ resin showed excellent thermal and flame retardant properties.

Bio-based phthalonitrile resin derived from quercetin as a sustainable molecular scaffold: Synthesis, curing reaction and comparison with petroleum-based counterparts

Synthesis, Curing, and Thermal Stability of Low-Temperature-Cured Benzoxazine Resins Based on Natural Renewable Resources

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis and Properties of a Novel Bio-based Benzoxazine

Sustainable synthesis of a novel bio-based low temperature curable benzoxazine monomer from quercetin: Synthesis, curing reaction and thermal properties

Natural magnolol derivatives as platform chemicals for bio-based phthalonitrile thermoset: Achieving high performances without an external curing agent

High-performance quinoxaline-containing phthalonitrile resin: Synthesis, curing kinetics, and properties

Recent Advances and Prospects in High‐Performance Bio‐Based Phthalonitrile Resins

Quercetin allylation and thiol–ene click photopolymerization to produce biobased polymer thermosets with robust thermomechanical properties

Bio-based epoxy resins derived from diphenolic acid via amidation showing enhanced performance and unexpected autocatalytic effect on curing

Catalytic Polymerization of Phthalonitrile Resins by Carborane with Enhanced Thermal Oxidation Resistance: Experimental and Molecular Simulation

Synthesis, characterization and self-promoted cure behaviors of a new phthalonitrile derivative 4-(4-(3, 5-diaminobenzoyl) phenoxy) phthalonitrile

Synthesis and properties of a sustainable, vanillin‐based phthalonitrile resin

Synthesis, Curing Kinetics, and Properties of a Novel Phthalazine‐Based Phthalonitrile Resin

Bio‐resourced eugenol derived phthalonitrile resin for high temperature composite

Synthesis of Pyridine Heterocyclic Low-Melting-Point Phthalonitrile Monomer and the Effects of Different Curing Agents on Resin Properties

A New Polycyclic Naphthoxazine Resin: Facile Synthesis, Characterization, Polymerization and Thermal Properties of Its Corresponding Thermosets

Bio-Based Epoxy-Phthalonitrile Resin: Preparation, Characterization, and Properties

Renewable biomass resources to access halogen- and phosphorus-free flame retardant thermosets with ultra-low heat release capacity

Novel Bio-Based Epoxy Thermosets Based on Triglycidyl Phloroglucinol Prepared by Thiol-Epoxy Reaction

A Pyridazine-Containing Phthalonitrile Resin for Heat-Resistant and Flame-Retardant Polymer Materials