Abstract:Due to its exceptional machinability, welding prowess, and resistance to corrosion, the lightweight 6061 Al–Mg–Si alloy finds extensive utilization within the realms of aerospace and transportation. Multi-directional forging process is a sever plastic deformation (SPD) process. In this investigation, a pristine 6061 industrial ingot was forged in multiple directions at 530 °C via four-upsetting and three-cross-stretching (4U3CS), seven-upsetting and six-cross-stretching (7U6CS), two different forging processes. T6 aging treatment is applied to the forged components after the pre-forging preparation. The investigation delved into the microstructural evolution during the process, alongside the mechanical performance across three orthogonal directions. The research findings underscore that, in comparison to 4U3CS, the cumulative deformation in 7U6CS fosters lattice distortion and defect formation, thereby promoting the dissolution of metastable phases and augmenting the driving force for precipitation during aging. Consequently, the tensile and yield strengths of the specimens increased by approximately 10 MPa across all three directions. Furthermore, 7U6CS retains a greater reservoir of deformation energy, acting as a catalyst for dynamic recrystallization, consequently, this process facilitates the enlargement of recrystallization nucleation regions and improves the degree of recrystallization uniformity. Following hot forging and subsequent T6 aging treatment, the disparity in grain size became more pronounced, diminishing from 418 to 208 μm. Coarse intergranular precipitates emerged as the primary origin of transgranular cracking. Post-T6 aging, the elongation rate of the specimens decreased across all three directions, accompanied by a substantial elevation in tensile and yield strengths. Notably, the mechanical performance of the 7U6CS-T6 specimen reached its zenith in the optimal direction, attaining values of 340 and 315 MPa for tensile strength and yield strength, respectively. Graphical

Effect of Grain Structure on Recrystallization Behavior of Al-Zn-Mg-Cu Alloy during Isothermal Forging

Development of Ultrafine Grain Structure in an Al–Mg–Mn–Sc–Zr Alloy During High-Temperature Multidirectional Isothermal Forging

Effect of Multidirectional Isothermal Forging on the Formation of Ultrafine-Grained Structure in Alloy 1570C

Effect of Forging on Microstructure and Properties of Al-9Si-5Cu-0.2Zr-0.1Sr-0.16Ti-0.1Ce Cast Aluminum Alloy

Influence of Forging Temperature on the Microstructures and Mechanical Properties of a Multi-Directionally Forged Al–Cu–Li Alloy

Microstructural and mechanical behavior of Al-Mg-Mn-Sc-Zr alloy subjected to multi-axial forging at room temperature

Grain Refinement Mechanism of 5A06 Aluminum Alloy Sheets during Cold Rotary Forging

Refinement mechanism of centimeter-grade coarse grains in as-cast Ti 2 AlNb-based alloy during multi-directional forging

Effect of Rotary Forging on Microstructure and Mechanical Properties of Mg–3Al–1Zn Magnesium Alloy

Influence of hot forging on grain formation in Al0.35CoCrFeNi high-entropy alloy: numerical simulation, microstructure and mechanical properties

Dynamic Recrystallization, Texture Evolution, and Improved Mechanical Properties of Mg-Y-Zn-V Alloy during Forging and Subsequent Extruding Deformation

Effect of initial grain size on hot deformation behavior and recrystallization mechanism of Al-Zn-Mg-Cu alloy

Effect of Cold Forging and Static Recrystallization on Microstructure and Mechanical Property of Magnesium Alloy AZ31

Static recrystallization and precipitation behavior of forged and annealed Mg–8.7Gd–4.18Y–0.42Zr magnesium alloy

Effect of Multidirectional Forging on the Microstructures and Mechanical Properties of the Al–Mg–Si Alloy

Preferential grain growth and textural evolution of AZ31B Mg alloy during annealing after isothermal compression at 400 °C

Dynamic recrystallization mechanisms of as-forged Al–Zn–Mg-(Cu) aluminum alloy during hot comp.ression deformation

Research on Grain Coarsening Mechanism of Forged 6061 Aluminum Alloy

Recrystallization behavior of an Al-Zn-Mg-Cu alloy during hot deformation and subsequent heat treatment

Microstructure evolution of an as-extruded WZ-A3 alloy during isothermal forging

Microstructure, Hot Deformation Behavior, and Recrystallization Behavior of Zn-1Fe-1Mg Alloy under Isothermal Compression