Improving the plateau performance of the TiZrFeMnCrV high-entropy alloy by partial substitution of V with fe, Mn and cr
Jinting Chen,Tingting Xu,Jinghan Zhang,Haixiang Huang,Jianguang Yuan,Bogu Liu,Bao Zhang,Ying Wu
DOI: https://doi.org/10.1016/j.matchemphys.2024.129219
IF: 4.778
2024-03-23
Materials Chemistry and Physics
Abstract:High-entropy alloys (HEAs) have shown desirable hydrogen storage performance owing to the lattice distortion effect and favorable phase structure. However, their pressure-composition-temperature (PCT) curves are usually lack of a well-defined hydrogen ab-/desorption plateau. Herein, we reported that by substituting 0.5 at.% Fe, Mn and Cr for the equivalent amount of V in the Ti 1.0 Zr 1.0 Fe 1.0 Mn 1.0 Cr 1.0 V 1.0 (defined as V 1.0 alloy) alloy, the plateau performance could be considerably improved. The non-equiatomic Ti 1.0 Zr 1.0 Fe 1.5 Mn 1.0 Cr 1.0 V 0.5 , Ti 1.0 Zr 1.0 Fe 1.0 Mn 1.5 Cr 1.0 V 0.5 and Ti 1.0 Zr 1.0 Fe 1.0 Mn 1.0 Cr 1.5 V 0.5 HEAs (defined as Fe 1.5 , Mn 1.5 and Cr 1.5 alloy, respectively) with a single C14 Laves phase rapidly absorb 1.82 wt%, 1.90 wt% and 1.89 wt% of hydrogen at 30 °C, respectively. Compare with the V 1.0 alloy, the Fe 1.5 , Mn 1.5 and Cr 1.5 alloys show clearly visible hydrogen ab-/desorption plateau. Among all the alloys, the Fe 1.5 alloy own the highest plateau pressure and hysteresis with values of 0.18/0.11 MPa and 0.41, followed by the Cr 1.5 alloy with values of 0.17/0.05 MPa and 0.38, and the Mn 1.5 alloy with values of 0.10/0.08 MPa and 0.28. Moreover, all the alloys exhibit good hydrogen ab-/desorption cycling performance, especially for the V 1.0 , Fe 1.5 and Mn 1.5 alloys, retaining 98, 99 and 97% reversible hydrogen storage capacity after 15 cycles, respectively.
materials science, multidisciplinary