Improved Toughness of a High‐Strength Low‐Alloy Steel for Arctic Ship by Ni and Mo Addition

Yong Tian,Jinhua Zhou,Yongfeng Shen,Zhizhong Qu,Wenying Xue,Zhaodong Wang

DOI: https://doi.org/10.1002/adem.201901553

IF: 3.6

2020-03-13

Advanced Engineering Materials

Abstract:The effect of Ni and Mo addition on the microstructures of a high strength low alloy (HSLA) steel under the TMCP process is currently unknown, which we explored by TEM and EBSD in this study. As the Ni increased from 0.6 to 0.9 wt. %, volume fraction of bainitic ferrite increased from 30% to 50%, average size decreased from 3 to 2 μm, and the size of martensite‐austenite (M‐A) constituent decreased from 1.2 to 0.7 μm. With increasing Mo from 0 to 0.2 wt. %, bainitic ferrite increased from 30% to 85%, and grain size increased from 3 to 5 μm. The size of M‐A constituent decreased from 1.2 to 0.3 μm. Impact absorbed energy at ‐100oC was increased from 50 to 70 J as the Ni increased from 0.6 to 0.9 wt. %, which decreased from 50 to 10 J with increasing Mo from 0 to 0.2 wt. %. The improved impact toughness was mainly resulted from the decreasing size of grain and M‐A constituent with the increasing Ni from 0.6 to 0.9 wt. %. In contrast, the decreasing impact toughness was resulted from the significantly increased grain size when the Mo content increased from 0 to 0.2 wt. %.This article is protected by copyright. All rights reserved.

materials science, multidisciplinary