A dislocation density-based model and processing maps of Ti-55511 alloy with bimodal microstructures during hot compression in α+β region

Yi-Wei Xiao,Y.C. Lin,Yu-Qiang Jiang,Xiao-Yong Zhang,Guo-Dong Pang,Dan Wang,Ke-Chao Zhou

DOI: https://doi.org/10.1016/j.msea.2020.139692

2020-07-01

Abstract:<p>Hot compression features of Ti-55511 alloy are investigated by high-temperature compression tests in α+β region. It is found that the flow stress and softening mechanisms are obviously influenced by deformation conditions. The true stress decreases with the reduced strain rate or the raised temperature. Furthermore, dynamic recrystallization easily occurs at low temperatures, while dynamic recovery (DRV) mainly occurs at high temperatures. A dislocation density-based constitutive model, which is associated with DRV, work hardening mechanisms and the spheroidization of α phases, is established and validated to describe flow behavior. The correlation coefficient (<em>R</em>) and average absolute relative error (<em>AARE</em>) of the established model are 0.9924 and 6.8%, respectively. 3D power dissipation efficiency maps and processing maps are established to determine the appropriate processing window, i.e., too low temperatures (lower than 973 K) or too high strain rates (higher than 1 s⁻¹) easily induce flow instability. Therefore, the medium temperature (1003–1063 K) and the low strain rate (0.001–0.1 s⁻¹) are applicable for thermal compression of the studied titanium alloy.</p>