Abstract:Surface layers of agricultural machinery working bodies are subjected to intensive abrasive wear during operation, which leads to rapid wear of equipment and reduction of its service life. To increase the wear resistance of the working surfaces of tools, the method of induction cladding using 'Sormait-1' materials is widely used. However, after coating, additional heat treatment is required, which improves physical and mechanical properties of the material and increases its durability. When using electrofriction technology (EFT) hardening, the surface of the parts is subjected to melting under the influence of electric arcs, which affects the surface characteristics of the coatings. In this work, two types of surface treatment of L53 steel were investigated: induction cladding using 'Sormait-1' material, as well as a combination of induction cladding and subsequent electrofriction treatment. The coatings were characterized and compared with the substrate in terms of the following parameters: microstructure, phase composition, hardness distribution, and friction-wear characteristics. After induction cladding of the Sormait-1 material, a dendritic structure was formed; however, subsequent electrofriction treatment resulted in a reduction of this dendritic structure, which contributed to an increase in the hardness of the material. The average hardness of the coatings after electrofriction treatment was 786 HV0.1, which is more than three times the hardness of the substrate. Furthermore, the influence of structural characteristics and hardness on abrasive wear resistance was examined in accordance with ASTM G65 international standards. Field tests were conducted on plough shares before and after electrofriction hardening to evaluate their performance. Each ploughshare was scanned with a structured 3D scanner before and after use in the field. From the scan data, the cutting-edge profile was calculated and three key parameters were determined: linear wear, volumetric wear, and mass reduction. According to the results of field tests, it was found that the service life of the blades hardened by electrofriction technology was 12%–14% higher compared to serial blades processed by induction cladding with the use of 'Sormait-1' material. Operational tests of hardened plough shares confirmed the results of laboratory tests and proved the advantages of electrofriction technology for increasing the wear resistance of soil tillage machine working bodies.

Reduction of Friction and Soil Adhesion of Medium Carbon Steel via Hard Coating and Surface Texture

Design for Manufacturing of Cemented Carbide Coated Components Toward High Wear and Impact Resistance Performance

Combined Effect of a Laser Cladded Coating and Surface Texture on Tribological Performance Under Dry Sliding and Starved Lubrication

Additional Tribological Effect of Laser Surface Texturing and Diamond-Like Carbon Coating for Medium Carbon Steel at Near Room Temperature

Anti-Wear Property of Laser Textured 42CrMo Steel Surface

Effect of Triangular Texture on the Tribological Performance of Die Steel with Tin Coatings under Lubricated Sliding Condition

Enhancing tribological performance of graphene sheet-embedded carbon films on steel substrates via texture engineering and chromium doping

Study on the Friction-Reducing Mechanisms of Surface Texture Cemented Carbide under Dry Sliding

Synergistic Effects of Ultrasonic Rolling Textures and PTFE‐PPS/SiO2 Coatings on Dry Friction and Wear Properties of GCr15 Steel Surfaces

Influence of Cr on the Surface Properties of the Micro-Textured WC+Co Alloy Coating

Analysis of Tribological Properties of Hardfaced High-Chromium Layers Subjected to Wear in Abrasive Soil Mass

Tribological Performance of Stearic Acid Film on Textured 45# Steel Substrate

Fabrication of AlTiN coatings deposited on the ultrasonic rolling textured substrates for improving coatings adhesion strength

Microstructure and Wear Resistance of FeCrV15 Coatings by Laser Cladding

Study on the surface performance strengthening of AlCrN coated cemented carbide by micro-texture laser preparation process

Microstructure, phase composition and wear properties of iron-based gradient coatings by laser cladding on 65Mn steel

Study on the role of chromium addition on sliding wear and corrosion resistance of high-manganese steel coating fabricated by wire arc additive manufacturing

Surface modification of ultrahigh strength 300M steel under supercritical carbon dioxide (scCO2)-assisted grinding process

Influence of Solid Chromizing Doped with Various Rare Earths on Microstructures and Properties of Cr-RE Coatings Fabricated by Pack Cementation

Increasing Wear Resistance of Ploughshare by Electrofriction Treatment

Effect Of Hybrid Surface Treatment Composed Of Plasma Nitriding And W-Cr-Ti-Al-N Coating On Tribological Behavior Of Aisi 316l Steel