Hot Deformation Behavior and Recrystallization Analysis of Pipe 20CrNiMo Steel
Jie Liu,Peng Zhang,Hailian Gui,Juan Li,Guanghui Zhao,Tong Xing,Hao Liu,Chen Zhang
DOI: https://doi.org/10.1007/s11665-024-10318-8
IF: 2.3
2024-11-03
Journal of Materials Engineering and Performance
Abstract:In this paper, the Gleeble−3800 testing machine was used to perform a hot compression test on a pipe made of 20CrNiMo steel with a deformation of 60%, within the temperature range of 1223 to 1423 K and at a strain rate of 0.01-10 s −1 . The stress-strain curve of pipe 20CrNiMo steel was analyzed, revealing that the flow stress decreased with increasing deformation temperature and decreasing strain rate. After analysis of the stress-strain data, the Arrhenius constitutive model for strain compensation was constructed. Using both the stress-strain data and the Arrhenius constitutive model, the hot processing map for pipe 20CrNiMo steel was established, identifying the better processing technology range for the pipe 20CrNiMo steel as 1357-1423 K/1.21-6.36 s −1 . Subsequently, the Electron Backscatter Diffraction (EBSD) technique was used to verify the hot processing technology results. In EBSD, it can be seen that the grain size of 20CrNiMo steel was grade 8 to grade 10 at 1357-1423 K/1.21-6.36 s −1 , and the grain size was not large. Simultaneously, using the stress-strain data, the recrystallization model was constructed. According to the recrystallization model and hot processing map, it is observed that the optimal processing temperature and strain rate for the pipe 20CrNiMo steel were determined to be 1365-1423 K and 1.21-3.71 s −1 , respectively.
materials science, multidisciplinary