Study of hydrogen storage properties of oxygen modified Ti- based AB2 type metal hydride alloy

M.W. Davids,T. Martin,M. Lototskyy,R. Denys,V. Yartys
DOI: https://doi.org/10.1016/j.ijhydene.2020.05.215
IF: 7.2
2021-04-01
International Journal of Hydrogen Energy
Abstract:<p>A multi component AB<sub>2</sub> type hydrogen storage intermetallic alloy (A = Ti<sub>0.85</sub>Zr<sub>0.15</sub>, B<sub>2</sub> = Mn<sub>1.22</sub>Ni<sub>0.22</sub>Cr<sub>0.2</sub>V<sub>0.3</sub>Fe<sub>0.06</sub>; was investigated in this work. The intermetallic specified above was modified by oxygen to yield the composition AB<sub>2</sub>O<sub>0.05</sub>. The oxygen was introduced by adding TiO<sub>2</sub> to the charge, with corresponding decrease of the Ti amount, followed by arc melting and annealing at the same conditions as for the oxygen free AB<sub>2</sub>-type alloy. The addition of oxygen to the alloy did not change much the PCT properties; the only difference was that the plateau pressure for the oxygen-modified alloy increased slightly. Both alloys have shown to be excellent candidates for H<sub>2</sub> storage, particularly for utility vehicles, due to their relatively high reversible H<sub>2</sub> storage capacity (1.6 wt%) and low plateau pressure at room temperature (&lt;5 bar). The addition of oxygen improved hydrogen absorption kinetics in the AB<sub>2</sub> alloy allowing it to immediately absorb H<sub>2</sub> without activation while for the non-modified sample an incubation period (30 min) was observed at the same conditions.</p>
energy & fuels,electrochemistry,chemistry, physical
What problem does this paper attempt to address?