Abstract:Phenomenological quality criteria extracted from a solidification and microstructure model known as InterDendritic Solidification are utilized to predict transverse cracking in peritectic C–Mn, low‐carbon B–Ti microalloyed, and peritectic Nb‐microalloyed steels during continuous casting with interpretable machine learning models. Balanced accuracies of 92%, 94.6%, and 82.8% indicate good predictive power, and interpretability enables the analyses of transverse cracking. The formation of defects such as cracks in continuous casting deteriorates the quality of cast products and efficiency of steelmaking. To evaluate the risks and identify the root causes of defect formation, phenomenological quality criteria computed with a solidification and microstructure model known as InterDendritic Solidification (IDS) have previously been applied. This approach is computationally efficient and provides a fundamental perspective to defect formation in continuous casting. The aim of this work is to study the capabilities of these criteria as features in predicting transverse cracking with interpretable machine learning models. IDS is coupled with a heat transfer model known as Tempsimu to simulate the continuous casting process. Measured compositions are utilized in the simulations and defects reported at a steelmaking plant are used as labels in classification. Logistic regression, decision tree, and Gaussian Naïve Bayes classifiers are developed to predict transverse cracking in peritectic C–Mn, low‐carbon B–Ti microalloyed, and peritectic Nb‐microalloyed steels. The corresponding balanced accuracies of the best classifiers from cross‐validation are 92%, 94.6%, and 82.8%. Due to the good performance and the interpretability of the developed classifiers, the fundamental causes of transverse cracking and possibilities of avoiding it by changes in the compositions are identified.

Experimental Quantification of Critical Parameters for Prediction of Surface Crack Formation in Continuous Casting

Simulation Analysis of Thermal Stress During Casting Process of Large-Sized Alloy Steel Ingot

Assessing the Effects of Steel Composition on Surface Cracks in Continuous Casting with Solidification Simulations and Phenomenological Quality Criteria for Quality Prediction Applications

Coupling of Solidification and Heat Transfer Simulations with Interpretable Machine Learning Algorithms to Predict Transverse Cracks in Continuous Casting of Steel

Towards Fully Automatic Modelling of the Fracture Process in Quasi-Brittle and Ductile Materials: a Unified Crack Growth Criterion

Numerical Modelling of Chamfer Billet of High Carbon Steel During Continuous Casting

A Novel Method for Characterizing the Fatigue Crack Propagation of Steel Via the Weak Magnetic Effect

Deformation and Damage Behavior of a 1Cr-Cast Steel Under Multiaxial Loading at Elevated Temperatures

Continuous Casting Mould for Square Steel Billet Optimised by Solidification Shrinkage Simulation

Prediction and Analysis on Formation of Internal Cracks in Continuously Cast Slabs by Mathematical Models.

Investigation of Corner Cracks in Continuous Casting Billet Using Thermomechanical Model and Plant Measurements

A Model for Diagnosing the Formation of Internal Cracks in Continuously Cast Slabs

Investigation and prediction of central cracking in cross wedge rolling

Evolution of Surface Crack on Slab During Rough Rolling Using Thermal-Mechanical FEM

Study on Surface Longitudinal Crack Formation of Typical Hypoeutectoid Steel Produced on a Caster with Billet and Slab

Optimization for Secondary Cooling Parameters in Continuous Casting of High Carbon Chromium Bearing Steel

Analysis and control of surface cracks in a B-bearing continuous casting blooms

The rolling simulation for cold work metal hardening

Fracture Prediction of Powder Metallurgical Fe–Cu–C Steel at Elevated Temperatures Via Finite Element-Aided Hot Tensile Tests

Numerical Simulation of Central Shrinkage Crack Formation in a 234-T Steel Ingot

Some Aspects of Continuous Casting of Low Carbon Microalloyed Steels with Niobium and Titanium