Abstract:Wood delignification can provide a wood-based template with sufficient pore volume for polymer/wood composites. At the same time, delignification is conducive to the penetration of polymer into the wood cell wall, which is of great significance to improve the function and performance of composites. However, lignin is the main chemical component in wood. The removal of lignin will inevitably lead to the change of the wood's physical properties, including the hygroscopicity of the wood. In this study, prepolymerized methyl methacrylate (MMA) impregnated delignified wood (DW) was used to obtain polymerized methyl methacrylate/delignified wood (PMMA/DW) composites with different lignin removal. The effect of lignin removal on the hygroscopicity of the composites is discussed. The results of nitrogen adsorption showed that the DW could adsorb more nitrogen than the original wood, and the amount of nitrogen adsorption gradually increased with the improvement of the processing degree. After filling with PMMA, the adsorption amount of nitrogen was greatly reduced. The results of the BET analysis showed that delignification promoted the distribution of PMMA in the pores of the wood cell wall. When lignin was almost completely removed, all mesopores in the cell wall were filled with PMMA. The results of the moisture absorption analysis isotherm curve showed that the moisture absorption content of the wood was positively correlated with the amount of lignin removed, and the moisture absorption content of the PMMA/DW composite was negatively correlated with the amount of lignin removed. The hygroscopic data were further analyzed using the Hailwood–Horrobin model. The results showed that the mole number of adsorbable or hydratable sites of the DW increased with the increase of lignin removal, and the situation of the PMMA/DW composites was just the opposite. In addition, after delignification, the dissolved water content and hydrated water content of the DW increased, and the increase was related to the delignification strength. The increase of dissolved water content indicates that the removal of lignin promotes the production of more volume in the cell wall, which provides space for the adsorption of multilayer water. After MMA in situ polymerization, the hydration and dissolved water content of the PMMA/DW decreased significantly, and the dissolved water content decreased even more significantly. The fitting curves of the H-H model and GDW model for the experimental data points of the differently treated samples were similar. The removal of lignin led to the increase of the w value, indicating that the ratio of water molecules adsorbed in the first layer of DW to the second layer increased, and the removal of lignin resulted in the enhancement of wood hygroscopicity; the opposite was true for the PMMA/DW.

Thermochemical and Mechanical Properties of Pine Wood Treated by In Situ Polymerization of Methyl Methacrylate (MMA)

Bulk Polymerization of PEGDA in Spruce Wood Using a DBD Plasma-Initiated Process to Improve the Flexural Strength of the Wood–Polymer Composite

Wood Flour-Reinforced Green Composites: Parameter Optimization via Multi-criteria Decision-Making Methods

Wood treatment using in situ polymerization of pine resin and styrene

In Situ Construction of Thermotropic Shape Memory Polymer in Wood for Enhancing Its Dimensional Stability

Manufacturing and Characterization of Modified Wood with In Situ Polymerization and Cross-linking of Water-Soluble Monomers on Wood Cell Walls

A new wood-modification process based on in situ grafting of urethane groups: biological resistance and dimensional stability of carbamylated Scots pine wood

Synthesis of lignin-g-MMA and the utilization of the copolymer in PVC/wood composites

Polymerised merbau extractives as impregnating material for wood properties enhancement

Synthesis Of Lignin-G-Mma And Its Utilization In Pvc/Wood Composite

Mechanical behaviour of chemically modified Norway spruce (Picea abies L. Karst.): Experimental mechanical studies on spruce wood after methacrylation and in situ polymerization of styrene

Superficial analysis of different wood polymer composites exposed to artificial weathering

Effect of MSU-J and Organic Modification on Mechanical and Thermal Properties of PMMA Hybrid Material

Investigate on the physical and mechanical properties of wood-polymer composition materials made on the premise of neighborhood wood flours

Effect of Thermal Modification on the Nano-Mechanical Properties of the Wood Cell Wall and Waterborne Polyacrylic Coating

Effect of Lignin Removal on the Hygroscopicity of PMMA/Wood Composites

Properties of patula pine plywood using phenolic resin-impregnated veneers

Enhancing green polyethylene composites with filler heat treatment: Pecan nutshells and Pinus sawdust impact

Mechanical properties of beech wood treated with malic acid-based polyester

Improvement in the Thermomechanical Properties and Adhesion of Wood Fibers to the Polyamide 6 Matrix by Sequential Ball Milling Technique

Poly(l-Lactic Acid)/Pine Wood Bio-Based Composites