Abstract:Janus particles have garnered significant attention due to their unique asymmetric structure. Researchers are dedicated to developing an industrial-scale production method for Janus particles. Herein, an oil-in-water emulsion was prepared through one-step mixing of functional monomer glycidyl methacrylate (GMA) and the fluorocarbon monomer (perfluorodecyl)ethyl acrylate (FC), which were simultaneously transformed into Janus particles (PFC–PGMA–NH2) with an epoxy group by ultraviolet (UV)-induced free radical polymerization. The incorporation of a composite surfactant solution, comprising sodium dodecyl sulfate (SDS) and a fluorocarbon surfactant (Zonyl FS-300), not only bolsters the stability of the emulsion but also confers control over droplet morphology. By manipulating the surface tension at the interface by varying the ratio of the surfactant to the monomer, fast and precise tuning of the internal droplet geometry was achieved from one-phase to two-phase PFC-in-PGMA/PGMA-in-PFC/Janus emulsions. The incorporation of active epoxy groups into the PFC–PGMA particles facilitates the selectively postfunctionalization reactions to produce amphiphilic PFC–PGMA–NH2 Janus particles. At the oil/water emulsion interface, the conversion rate of the gold-loaded PFC–PGMA–NH2@Au Janus catalyst reached 84.13% after 2 h, exhibiting a remarkable enhancement of 12.7 times compared to that achieved through oil–water two-phase interface catalysis under identical reaction conditions. As solid amphiphilic surfactants, Janus particles with precisely adjustable hydrophilic/hydrophobic properties exhibit exceptional capabilities in stabilizing emulsions. Therefore, they play a crucial role in enhancing catalytic efficiency and regulating active sites during two-phase catalysis. They are expected to be used in protein immobilization, interfacial biocatalysis, and other fields.

Preparation of amphiphilic Janus SiO2 particles and its application on polyacrylate emulsion

Synthesis Of Cationic Surface Sizing Agent And Its Application

Synthesis and properties of alkoxysilane-modified acrylic latex via miniemulsion polymerization

Study on Silicone Modified Polyurethane-Acrylate Copolymer Emulstion

Hydrophobicity of Polyacrylate Emulsion Film Enhanced by Introduction of Nano-SiO₂ and Fluorine

Properties and Characterization of Novel Cationic Polyacrylate Latex Containing Fluorine and Silicon Prepared with Soap-Free Emulsion Polymerization

Efficient Fabrication of Janus Particles with Active Groups and Application in Emulsion Stabilization and Interfacial Catalysis

Anchoring of polyacrylate onto silica and formation of polyacrylate/silica nanocomposite particles via in situ emulsion polymerization

Characterization and Particle Size Control of Acrylic Polymer Latex Prepared with Green Surfactants

Emulsion Interfacial Synthesis of Asymmetric Janus Particles

Preparation of Asymmetric Al2O3-SiO2 Janus Nanoparticles in Aqueous Phase and Its Interfacial Property

Preparation of acrylate polymer/silica nanocomposite particles with high silica encapsulation efficiency via miniemulsion polymerization

Electrostatic Absorption of Initiator Onto Nanometer SiO2 Particles and In-Situ Emulsion Polymerization of Methyl Methacrylate in the Presence of Modified Nanometer SiO2

Amphiphilic Janus Microspheres Prepared by Caged Photoactivatable Alkoxysilane

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Equilibrium and self-assembly of Janus particles at liquid-liquid interfaces for the film formation

Preparation and characterization of self-crosslinking acrylate emulsion modified by divinyl silane

Facile fabrication of superhydrophilic poly(styrene-co-acrylate)/SiO2 composite materials by conventional emulsion polymerization

Hydrophobicity of Polyacrylate Emulsion Film Enhanced by Introduction of Nano-SiO<sub>2</sub> and Fluorine

Preparation of a Fluorocarbon Polymerizable Surfactant and Its Application in Emulsion Polymerization of Fluorine-Containing Acrylate

Hydrophobicity of Polyacrylate Emulsion Film Enhanced by Introduction of Nano-SiO2 and Fluorine