Abstract:Abstract GLARE laminates have emerged as a favored option for the construction of fuselage and wing skins in large airliners, owing to their exceptional mechanical characteristics. Nevertheless, the incorporation of open‐hole designs poses a challenge as it disrupts the continuity of the laminates, resulting in stress concentration and subsequent damage. To investigate the impact of various layup orientations and hole sizes on the tensile properties of open‐hole GLARE laminates, this study conducted axial tensile tests. Additionally, the tensile damage process was monitored using DIC and AE techniques, enabling the identification of damage patterns and the analysis of their evolution. The results demonstrate a noteworthy decline in the ultimate strength and failure strain as the size of the opening increases. Moreover, the retention rate of failure strain displays a marked sensitivity to the layup orientation. In conjunction with observations made through DIC and SEM, the k‐means++ algorithm successfully clustered peak frequencies, thereby revealing distinct damage patterns and their corresponding frequency ranges as aluminum alloy damage [0–90 kHz], matrix cracking [104–174 kHz], fiber/matrix debonding [175–224 kHz], interlaminar delamination [234–300 kHz], and fiber fracture [304–469 kHz]. AE cumulative counts were utilized to evaluate the progression of individual damage modes. The results emphasize that matrix cracking demonstrates the most substantial cumulative counts, whereas damage to the fibers and aluminum alloy noticeably affects the load‐carrying capability of the laminate. Furthermore, the fibers/matrix debonding and interlaminar delamination, exhibit heightened susceptibility to layup orientation and hole size. Highlights The tensile performance evaluation of GLARE laminates with open‐hole varying layup orientations and hole sizes was investigated. A combination of DIC and AE techniques was used to monitor the tensile damage process. Damage pattern was identified based on the observations of DIC and SEM. An approach based on Pearson's correlation coefficient and k‐means++ clustering algorithm was used for damage pattern recognition in GLARE laminates. AE cumulative counts were employed to assess the evolution of each damage mode.

Stress state failure analysis of thin-walled GLARE composite members subjected to axial loading in the post-buckling range

Micro Failure Analysis of Fiber Metal Laminates

Progressive Failure Analysis of Thin-Walled Composite Structures Verified Experimentally

Experimental-Numerical Failure Analysis of Thin-Walled Composite Columns Using Advanced Damage Models

Finite Element Analysis of the Fatigue Crack Tip Parameters in the Glass Fiber Reinforced Aluminum Alloy Laminates under Tension-Compression Loading

Finite element analysis of dynamic progressive failure properties of GLARE hybrid laminates under low-velocity impact

Comparative study of failure analysis in glass fiber reinforced laminated pin joints under cyclic and static loading conditions

Short beam shear damage analysis of GLARE laminates based on digital image correlation and finite element analysis

Failure analysis and experimental study on bolted composite joints based on continuum damage mechanics

Stability and Failure of Thin-Walled Composite Plate Elements with Asymmetric Configurations

Experimental study for the effect of hole notched in fracture mechanics of GLARE and GFRP composites subjected to quasi-static loading

De Lamination And Fatigue Crack Growth Behavior In Fiber Metal Laminates (Glare) Under Single Overloads

Strength Analysis Methods for High Stress Gradient Parts in Composite Structures Ensuring Design Office Requirements

Characterizing damage patterns and evolution in Multi-Hole GLARE laminates under tensile load via integrated AE and DIC techniques

Failure Analysis of Carbon Fiber Reinforced Composite Subjected to Low Velocity Impact and Compression after Impact

A Combined Experimental and Computational Analysis of Failure Mechanisms in Open-Hole Cross-ply Laminates under Flexural Loading

Failure Analysis of Hat-Stringer-Stiffened Aircraft Composite Panels under Four-Point Bending Loading

Buckling Analysis of Thin-Walled Composite Structures with Rectangular Cross-Sections under Compressive Load

Progressive failure simulation of angled composite beams subject to flexural loading

Load-Carrying Capacity of Thin-Walled Composite Columns with Rectangular Cross-Section under Axial Compression

Assessment of tensile damage mechanism of open‐hole GLARE laminates based on acoustic emission and digital image correlation techniques