Abstract:This paper is to study the influence of sulphate corrosion on the mechanical behaviors of concrete, especially concrete corrosion under actual corrosion environment. This study investigated different immersion methods for concrete in a corrosion environment, and different strengths of concrete specimens with contents of sodium sulphate and magnesium chloride of 10.36% and 12.00%, respectively. Strength tests were performed on the specimens for the different immersion methods of full immersion, half-immersion, and dry-wet cycles, and with different strengths for the concrete of C20, C35, and C50. To study the internal mechanisms of the corrosion of concrete with different immersion methods and different strengths, a microscopic pore structure test was conducted. The field tests were performed after 12 years to evaluate the long term performance of the concrete under the actual environmental conditions. The test results show that full immersion mainly led to chemical corrosion, half immersion led to double damage from salt crystallization and chemical corrosion, and dry-wet cycles accelerated the corrosions of the salt crystallization and chemical corrosion. The higher the strength of concrete, the better its resistance to the sulphate corrosion. In comparison with the strength of the concrete before corrosion, field test results show that the strength of uncorroded concrete after 12 years is increased by 9.5% and the strength of corroded concrete after 12 years is reduced by 56.2%. The results of the strength tests and pore structure tests show that sulphate has a significant impact on concrete strength after 12 years of field tests. This study will contribute to improve long-term performance of the concrete, provide guidance for concrete structure design in corroded areas, and suggested that increasing attention should be paid to the effects of sulphate on concrete performance.

Experimental Study and Analysis on the Durability of Concrete in Underground Engineering

Experimental Study On Permeability And Chloride Resistance Properties Of Concrete In Yu-Cheng Bridge

EXPERIMENTAL ENHANCEMENT STUDY ON DURABILITY OF CONCRETE IN WHARF PROJECT

Study on Durability of Concrete in Coal Mine

Study on Relation Between Early-age Performance of Concrete and Its Durability

Optimal Design and Performance of Concrete with Function Component in Marine Environment

Effecting Coefficients for Concrete Structure Durability Design Index

Accelerating Tests For The Performance Deterioration Of Concrete Exposed To Chloride Media

Study on the Durability of Concrete under an Underwater Coupling Environment

Experimental Study on Chloride Ion Transport in Concrete Structure under Shear Stress

Experimental study on underground structure concrete under static bending loads and sulfate attack

Research on Durability of Concrete Cube Piles under the Coastal Soil Condition

Grading the Environmental Area According to Its Effect on the Durability of Concrete Structures under Atmospheric Condition

Durability of the Concrete Pile in the Coastal Soil Environment

Evaluation of the Performance of Surface Treatments on Concrete Durability

Influence mechanisms under different immersion methods and different strengths of concrete in corrosive environments, and verification via long-term field test

Durability evaluation of concrete made of fly ash and copper slag

Durability Of Concrete Under Coupling Effects Of Cyclic Loads And Chloride Environment

Durability Performance and Corrosion Mechanism of New Basalt Fiber Concrete under Organic Water Environment

Study on strength and durability of fair-faced concrete in underground station of urban rail transit

Combined effect of abrasion of sediment-laden flow and chloride ions penetration on the durability of concrete