Abstract:Cross-linked polyethylene(XLPE) insulating materials are widely used in the medium and high voltage cables because of their excellent electrical performances, as well as stable physical and chemical properties. With the long-term running of the XLPE cables, some degradation reactions of the insulating materials will happen under the action of long time thermal stress, which cause the irreversible changes for the chemical structure and morphology of these types insulating materials. The aging degradation will weaken the electrical properties of the cables and lead to insulation failure gradually, which brings about irreparable damage to the society and people. In this paper, both the resisting water tree and ordinary XLPE cable materials were selected as the study object, the aging temperature were set at 110°C, 130°C, 150°C to conduct accelerated aging experiments on the resisting water tree and ordinary XLPE cable materials, respectively. The effects of thermal aging on mechanical properties and electrical resistance of these XLPE insulation materials were studied, including the infrared transmission spectroscopy, the gel content, the tensile strength test and AC breakdown strength test and so on. The experimental results show that the tensile strength of the studied insulation materials increased firstly and then decreased at the selected aging temperatures. From 0 to 500 h of the aging time, the tensile strength of the two materials had a rising trend. The higher the aging temperature, the shorter the time to the turning point of the tensile strength. With the aging time prolonging, the tensile strength of both materials both decreased. And the tensile strength of the anti-water tree XLPE material was higher than that of ordinary XLPE. There exited significantly different with the absorption peak for both type XLPE materials in the 1000 cm -1 , which was due to the introduction of new functional groups to XLPE by the anti-water tree additive. As the aging temperature increased and the aging time was prolonged, the aging degree of ordinary XLPE materials was more severe than that of the antiwater tree XLPE insulation materials. The gel content of the two XLPE insulation materials increased firstly and then decreased with the increase of the thermal temperature and corresponding aging time, which shows that the cross-linking degree of the two XLPE increases first and then decreases. With the increase of the aging temperature and the aging time, the carbonyl index significantly increased for aged ordinary XLPE materials. However, the carbonyl index of the anti-water tree XLPE insulating materials changed smaller than that of the ordinary ones. Therefore, the anti-water tree XLPE insulating materials have better ability to inhibit thermal aging.

Effects of electrical aging on the structural and physicochemical properties of crosslinked polyethylene (XLPE) cable insulation material

Investigation on Thermal Aging and Degradation of XLPE for High Voltage Cable Applications

Effect of Tensile Stress on Insulation Properties of 500 Kv EHVAC XLPE Cable under Multi-Field Ageing

Influence of Thermal Aging on Insulation Properties of Voltage Stabilizer Blended Cross-Linked Polyethylene

The Effect of DC Electro-thermal Ageing on Electrical Treeing in Polyethylene

Effect of Thermal Ageing on Insulation Properties of 500 Kv DC XLPE Submarine Cable Insulation

Effect of Thermal Aging on the Physicochemical Structure of XLPE Cable Insulation

Evolution of Dielectric Properties of Cross-Linked Polyethylene under Thermal-Oxidative Aging

Influence of Thermal Ageing on the Optical Performance of XLPE Cable Insulation

Aging characteristics of 110kV crosslinked polyethylene cable insulation materials

Research on the Thermal Aging Characteristics of Crosslinked Polyethylene Cables Based on Polarization and Depolarization Current Measurement

Effects of Thermal Aging on the Crystal Structures of the XLPE Cable Insulating Material at Different Temperatures

Effect of Thermal Aging on Mechanical and Physical Performances of Resisting Water Tree XLPE

Study of Dielectric Response Characteristics for Thermal Aging of XLPE Cable Insulation

Influence of Oxygen Diffusion on Thermal Ageing of Cross-Linked Polyethylene Cable Insulation

Different Oxygen Diffusion Patterns in XLPE under Thermal Oxidative Aging

Changes on structural and electrical properties of retired cross-linked polyethylene (XLPE) cable insulation under electro-thermal aging test

Aging Phenomena in Non-Crosslinked Polyolefin Blend Cable Insulation Material: Electrical Treeing and Thermal Aging

Aging and life control of cross-linked polyethylene for cable insulation material

Effect of thermo-oxidative aging on thermal elongation performance of XLPE insulation for high-voltage cables

Influence of Thermal Aging on Space Charge Characteristics and Electrical Conduction Behavior of Cross-Linked Polyethylene Cable Insulation