Smart functionalization of PEO coating on AZ31B magnesium alloy by a novel facile one-step sealing method
Ning Li,Ning Ling,Haoyuan Fan,Kang Liang,Jinglai Zhang,Li Wang
DOI: https://doi.org/10.1016/j.surfcoat.2023.129674
IF: 4.865
2023-06-05
Surface and Coatings Technology
Abstract:Plasma electrolytic oxidation (PEO) coating has been widely applied for the magnesium alloys to resist the corrosion. However, the defaults on the PEO surface greatly weaken its long-term anti-corrosion performance. To fill the micropores is an efficient and feasible strategy to refine the compactness and anti-corrosion of PEO coating and achieve the additional function. Although various sealing pathways are reported in past decades, the leakage of filler and long-term anti-corrosion performance are still the perplexing issues. The corrosion inhibitor 1-methyl-3-(carboxyundecyl)imidazolium bis(trifluoromethylsulfonyl)imide ([MCIM][NTf 2 ], MN), is grafted on the clinochrysotile-like magnesium silicate nanotubes (MSNTs) by the post-synthesis method, then, the is filled into the micropores on the PEO surface by the post-sealing process to form PEO/ According to the electrochemical results in 3.5 wt% NaCl solution, the log |Z| 0.01Hz is increased by 1.26 times after the sealing. After immersion in 3.5 wt% NaCl solution for 120 h, the log |Z| 0.01Hz of PEO/ is still the 1.56 times larger than that of PEO. The PEO coating filled by the offers the consistently superior corrosion resistance up to 336 h of salt spray tests with 5.0 wt% NaCl solution. The superior anti-corrosion performance of PEO/ is associated with the cooperation of physical barrier of PEO coating and protection from The grafted corrosion inhibitor would not leak easily, which is favorable to achieve the long-term anti-corrosion performance. The immobilized MN provides the active anti-corrosion in the initial corrosion stage achieving the self-healing function. Moreover, the release of corrosion inhibitor, MN, does not rely on the smart trigger, which broadens the scope of immobilized materials. This work introduces a facile and one-step strategy to seal the pores on the PEO surface with the self-healing function and improved anti-corrosion capability.
physics, applied,materials science, coatings & films