Corrosion resistance of Mg−Al LDH/Mg(OH)2/silane−Ce hybrid coating on magnesium alloy AZ31

Zai-meng QIU,Rong-chang ZENG,Fen ZHANG,SONG Liang,Shuo-qi LI,Liang SONG
DOI: https://doi.org/10.1016/s1003-6326(20)65435-8
IF: 3.752
2020-11-01
Transactions of Nonferrous Metals Society of China
Abstract:An environmentally-friendly hybrid coating on AZ31 magnesium alloy substrates was reported. The synergic effect was studied on Mg−Al-layered double hydroxide Mg−Al LDH/Mg(OH)<sub>2</sub>-coated AZ31 magnesium alloy via an in-situ steam coating process and a subsequent combined surface modification of bis-[triethoxysilylpropyl]tetrasulfide (BTESPT) silane and Ce(NO<sub>3</sub>)<sub>3</sub>. The microstructure and composition characteristics of the hybrid coatings were investigated by means of X-ray diffraction (XRD), scanning electronic microscopy (SEM), Fourier transform infrared spectrophotometry (FT-IR) and X-ray photoelectron spectroscopy (XPS). The corrosion resistance of the coated samples was evaluated by potentiodynamic polarization (PDP), electrochemical impedance spectrum (EIS) and hydrogen evolution rate during immersion in 3.5 wt.% NaCl solution. The results show an improved corrosion resistance of the alloy in the presence of BTESPT silane and Ce(NO<sub>3</sub>)<sub>3</sub>. This is most likely due to the synergistic effect of steam coating and silane coating to enhance the barrier properties of hybrid coating. In addition, the formation mechanism and anti-corrosion mechanism of coatings were discussed.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?
This paper mainly discusses methods to improve the corrosion resistance of magnesium alloy AZ31. The researchers used an in-situ steam coating process to generate Mg-Al layered double hydroxide (LDH)/Mg(OH)2 composite coating on the surface of the magnesium alloy, and further combined bis(3-triethoxysilylpropyl) tetrasulfide (BTESPT) and Ce(NO3)3 for surface modification to prepare a mixed coating. The microstructure and composition of the coating were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FT-IR), and X-ray photoelectron spectroscopy (XPS). The experimental results show that the mixed coating with BTESPT and Ce(NO3)3 significantly improves the corrosion resistance of the magnesium alloy. This is attributed to the synergistic effect of the steam coating and silane coating, which enhances the barrier properties of the composite coating. In addition, the formation mechanism and corrosion protection mechanism of the coating are discussed. Corrosion evaluation shows that the corrosion current density of the coated samples is significantly reduced in a 3.5 wt.% NaCl solution, and electrochemical impedance spectroscopy (EIS) and hydrogen evolution rate test also confirm its excellent corrosion resistance. In conclusion, this paper proposes a new environmentally friendly corrosion-resistant mixed coating, which effectively enhances the corrosion resistance of magnesium alloy by optimizing the coating structure and introducing Ce inhibitor.