Abstract:Mn–Cr–O spinel catalysts (MnCr2O4 and Mn1.5Cr1.5O4) and single oxides of Mn and Cr are coked under ethylene and ethylene–steam mixtures to simulate reaction conditions occurring in steam cracker furnaces. The coking rates are measured using thermogravimetric analysis, and the Mn1.5Cr1.5O4 catalyst displayed considerably less coke deposition (an order of magnitude) under ethylene–steam flow. Analysis of the outlet gas flow suggests the Mn1.5Cr1.5O4 catalyst gasified the radically formed coke into carbon oxides without significantly affecting ethylene conversion. The anticoking performance of the Mn1.5Cr1.5O4 catalyst is attributed to the presence of Mn3+ species in the spinel phase structure that are active for coke gasification in the presence of steam. No significant changes in structure or performance are observed for the Mn1.5Cr1.5O4 catalyst across several coking and decoking cycles. The Mn–Cr–O spinel oxide with higher Mn content is suggested to have desirable activity and stability to limit coke deposition during steam cracking.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.1c00036?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.1c00036</a>.Figures S1, TG profiles of coked crucible; Figure S2, SEM images; Figure S3, CO/CO2 during crucible decoking; Table S1, catalyst physical properties; Table S2, coking rates summary; Tables S3 and S4, additional product gas analysis; Figures S4 and S5, additional XRD patterns; and Table S5, spinel compositions and lattice constants after Rietveld refinement (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.1c00036/suppl_file/ef1c00036_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Spinel-type MnxCr3-xO4-based catalysts for ethanol steam reforming

Mechanism of Ethanol Steam Reforming Over Pt/(Ni+Ru)-Promoted Oxides by FTIRS In Situ

Methanol Steam Reforming on Metal–Carbon Catalysts Having Different Carbon Supports

Performance of nickel-manganese and nickel-cobalt-manganese mixed oxide catalysts in ethanol total oxidation

Novel spinel oxide catalysts CuFexAl2−xO4 with high H2 selectivity with low CO generation in methanol steam reforming

ZnFexAl2-xO4 spinel supported PdZnβ bifunctional catalyst for methanol steam reforming

Boosting Catalytic Combustion of Ethanol by Tuning Morphologies and Exposed Crystal Facets of α-Mn2O3

Supported platinum–zinc oxide core–shell nanoparticle catalysts for methanol steam reforming

Mesoporous Silica Encapsulated Core-Shell NiRh@NiO Nanocatalyst for Performance-Enhanced Ethanol Steam Reforming

Ambient pressure XPS and IRRAS investigation of ethanol steam reforming on Ni-CeO2(111) catalysts: an in situ study of C-C and O-H bond scission

Enhanced Coke Gasification Activity of the Mn 1.5 Cr 1.5 O 4 Spinel Catalyst during Coking in Ethylene–Steam Mixtures

Steam reforming of ethanol over Ni/MgAl2O4 catalysts

Molecular Catalysis for the Steam Reforming of Ethanol

Modification of CuO–ZrO2–ZnO Mixed Oxide Catalyst with Mn, Ga, Ni: Impact on Physicochemical Properties and Hydrogen Production via Low Temperature Steam Reforming of Ethanol

Fe–Ni–Ce–Zr-modified CuO–ZnO catalyst for methanol steam reforming

Global Vision of the Reaction and Deactivation Routes in the Ethanol Steam Reforming on a Catalyst Derived from a Ni-Al Spinel

Cu–Mn–O nano-particle/nano-sheet spinel-type materials as catalysts in methanol steam reforming (MSR) and preferential oxidation (PROX) reaction for purified hydrogen production

Cu1−xMgxAl3 spinel solid solution as a sustained release catalyst: One-pot green synthesis and catalytic performance in methanol steam reforming

Waste-free Soft Reactive Grinding Synthesis of High-Surface-Area Copper–Manganese Spinel Oxide Catalysts Highly Effective for Methanol Steam Reforming

Mesoporous Manganese-Cobalt Oxide Spinel Catalysts for CO2 Hydrogenation to Methanol

Steam reforming kinetics of olefins and aromatics over Mn-Cr-O spinel oxides