Microwave dielectric properties of BaWO4-doped Ba(Mg1/3Nb2/3)O3 ceramics

Sen Peng,Jianming Xu

DOI: https://doi.org/10.1007/s10854-020-04720-w

2020-10-28

Abstract:In this paper, Ba(Mg_1/3Nb_2/3)O₃ (BMN) ceramics with <i>x</i> (<i>x</i> = 0–9) wt% BaWO₄ were synthesized using the conventional solid-state sintering technique. Effects of BaWO₄ addition on the microstructure and microwave dielectric properties of BMN ceramics were evaluated. X-ray diffraction (XRD) analysis showed that there were three phases: main crystalline phase Ba(Mg_1/3Nb_2/3)O₃ and secondary phases BaWO₄ and Ba₅Nb₄O₁₅. Meanwhile, the (100) super-lattice reflection peaks shifted to a higher 2θ angle with increasing BaWO₄ content. SEM photographs suggested that BaWO₄ working as a sintering additive promoted the densification and grain growth. The dielectric properties were examined by Vector network analyzer. The dielectric constant (ε_<i>r</i>) was largely determined by the relative density and phase composition. Meanwhile, the addition of BaWO₄ had a positive effect on the <i>Q</i> × <i>f</i> value, for example the specimen with <i>x</i> = 5 possessed the highest <i>Q</i> × <i>f</i> value of 111,300 GHz. Optimum microwave dielectric properties (ε_<i>r</i> = 31.7, <i>Q</i> × <i>f</i> = 111,300 GHz (<i>f</i> = 8 GHz) and τ_<i>f</i> = 0.16 ppm/°C) were obtained for the specimen with <i>x</i> = 5 sintered at 1350 °C for 6 h.