Abstract:Here, staple carbon fiber fabric-reinforced polycarbonate (PC)- and epoxy (EP)-based composites with different impregnating resin levels were fabricated using a modified film stacking process. The effects of surface topographies and resin types on the tribological properties of stable carbon fabric composites (sCFC) were investigated. Friction and wear tests on the carbon composites were conducted under unlubricated sliding using a disk-on-disk wear test machine. Experimental results showed that the coefficient of friction (COF) of the sCFC was dominated by matrix type, followed by peak material portion (Smr1) values, and finalized with core height (Sk) values. The COF of composites decreased by increasing the sliding speed and applied pressure. This also relied on surface topography and temperature generated at the worn surface. However, the specific wear rate was strongly affected by resin impregnation. Partially-impregnated composites showed lower specific wear rate, whereas fully-impregnated composites showed a higher wear rate. This substantially increased by increasing the sliding speed and applied pressure. Scanning electron microscopy observations of the worn surfaces revealed that the primary wear mechanisms were abrasion, adhesion, and fatigue for PC-based composites. For EP-based composites, this was primarily abrasion and fatigue. Results proved that partially-impregnated composites exhibited better tribological properties under severe conditions.

The friction and wear behaviors of self-lubricating composites with two types of warp-knitted fabric structures

Wear failure mechanism analysis of self-lubricating fabric composites at high temperature

The tribological properties of multilayer hybrid PTFE/Nomex fabric/phenolic resin composite with two fabric structure under water lubrication

Understanding friction and wear properties of carbon fiber/epoxy stitched composites

Study on the Friction and Sliding Wear Behavior of Hybrid Polytetrafluoroethylene/Kevlar Fabric Composites Filled with Polyphenylene Sulfide

Enhancement of the Water-Lubricated Tribological Properties of Hybrid PTFE/Nomex Fabric Laminate Composite via Epoxy Resin and Graphite Filler

Nonuniform Wear Mechanism of Kevlar/Polytetrafluoroethylene Fiber-Reinforced Composites

Influence of fabric geometry on yarn pull‐out property and wear performance of hybrid S‐glass/ PTFE fabric‐reinforced composites

Synchronously improved thermal conductivity and tribological performance of self-lubricating fabric liner composites via integrated design method with copper yarn

Combined effects of interface modification and micro-filler reinforcements on the thermal and tribological performances of fabric composites

The mechanical and tribological properties of aramid (Twaron) fabric/polytetrafluoroethylene composites

Tribological properties of PTFE/Kevlar fabric composites under heavy loading

Tensile and Tribological Properties of Ptfe and Nanoparticles Modified Epoxy-Based Polyester Fabric Composites

Mechanical Prediction and Experimental Verification of Self-Lubricating Fabric Composites

Tribological behavior of PTFE/Nomex/phenolic composite lubricant under cold forming condition in the bearing assembly process

Preparation and tribological behavior of polytetrafluoroethylene/metal mesh composites with sandwich structure

A Study on the Mechanical and Tribological Properties of Carbon Fabric/PTFE Composites

Wear mechanism of Nomex/PTFE fiber reinforced composites

Friction and Wear Behavior of PTFE Coatings Modified with Poly (methyl Methacrylate)

Experimental investigation on dry frictional behavior of the two self-lubricating composites under heavy loading conditions

Friction and Wear Performance of Staple Carbon Fabric-Reinforced Composites: Effects of Surface Topography