Abstract:A novel pathway for the magnesiothermic reduction of boron oxide and magnesium dodecaboride (MgB12) in the presence of carbon by a self-propagating high-temperature synthesis method was proposed that was aimed at the direct preparation of boron carbide nanopowder. The combined utilization of two boron sources, boron oxide and MgB12, allowed tailoring the overall caloric effect of the process, increasing the yield of the target product and lessening the laborious leaching process. In addition, it is an alternative way to utilize magnesium borides, which are inevitable side products at boron production. Multivariate thermodynamic calculations performed in the B2O3-MgB12-Mg-C system allowed estimating equilibrium compositions of the products and deducing the optimum composition of the initial mixture for obtaining B4C. For the latter, the adiabatic temperature (Tad) is 2100 °C, which is theoretically enough for the implementation of the self-propagating reaction. The combustion reaction was shown to be extremely sensitive to the initial mixture composition, external pressure, as well as sample diameter (heat losses). It proceeds in self-oscillatory mode and leads to the product of a layered macrostructure. The combustion product was then consolidated by the spark plasma sintering technique at different conditions. Vickers microhardness was measured, and the wear erosion behavior was examined. The variation in lattice parameters of boron carbide reflected the influence of synthesis, sintering and erosion conditions on the ordering/disordering of the boron carbide structure.

Microwave-assisted Preparation of Precursor for the Synthesis of Nanocrystalline Boron Carbide Powder

Preparation of Submicron Boron Carbide Powder Through Gas-Solid Reaction Method

The Hydrothermal Method of Preparing Boron–Saccharide Precursors for the Synthesis of Boron Carbide and Its Influence on the Morphology and Phase Composition of the Obtained Products

Construction of a Nanoporous Highly Crystalline Hexagonal Boron Nitride from an Amorphous Precursor for Catalytic Dehydrogenation.

Novel Pathway for the Combustion Synthesis and Consolidation of Boron Carbide

Preparation and Characterization of Nanocrystalline Chromium Boride

Synthesis of Boron Carbide Powder Through Gas-Solid Reaction Method Using Nanoporous Carbon As Carbon Source

Low-temperature synthesis of high-purity boron carbide via an aromatic polymer precursor

Synthesis of Boron and Boride Compounds Nanowire Arrays by Chemical Vapor Deposition

LOW-TEMPERATURE PREPARATION OF NANO-CRYSTALLINE LITHIUM NIOBATE POWDERS BY THE POLYMERIC PRECURSOR METHOD

Production of boron carbide powder by carbothermal synthesis of gel material

Carbothermal Reduction Synthesis Of Zirconium Diboride Powders Assisted By Microwave

Additive-assisted synthesis of boride, carbide, and nitride micro/nanocrystals

Preparation of Amorphous Si-B-C-N Powders and Nano-Sized Ceramics

Preparation of Nano-Zrb2 Powder by Ca Liquid Assisted Boronation Reaction Between ZrC and B4C

Synthesis of Nanocrystalline Boron Carbide Via a Solvothermal Reduction of CCl4 in the Presence of Amorphous Boron Powder

Preparation of novel carborane-containing boron carbide precursor and its derived ceramic hollow microsphere

Preparation and Structure of Boron Carbide Nanowires

A General Route for the Convenient Synthesis of Crystalline Hexagonal Boron Nitride Micromesh at Mild Temperature

Combustion synthesized boron carbide powders by different organic carbon sources and microwave absorbing properties

Fast Synthesis of Fine Boron Carbide Powders Using Electromagnetic Induction Synthesis Method