Hybrid effect of nano-alumina and nano-titanium dioxide on Mechanical properties of concrete

Muhammad Atiq Orakzai

DOI: https://doi.org/10.1016/j.cscm.2020.e00483

IF: 4.934

2021-06-01

Case Studies in Construction Materials

Abstract:This paper investigates the effect of the binary combination of nano-alumina (nano-Al₂O₃) and nano-titanium dioxide (nano-TiO₂) on the mechanical properties of concrete. Although many studies support the addition of nano-particles to make optimal the use of concrete in building structures, singularly as well as in combination, the author endeavors, below, to codify such anecdotal evidence. The objective of this research is to study the effect of more than one nano-particle on the mechanical properties of concrete. The dosage of nano-particles remained within a range of 0.5-2 wt% relative to the cement. Compressive and splitting tensile strength tests were conducted on 100 mm x 200 mm cylinders followed next by the flexural strength test performed on 150 mm x 150 mm x 450 mm beams after 28 days curing period. The results suggest that the binary combination of nano-Al₂O₃ and nano-TiO₂ lead to compact and dense microstructure with fewer intermittent pores. The optimum dosage for nano-Al₂O₃ and nano-TiO₂ found was 0.5% and 1% by weight of cement respectively. When compared with the control sample, the compressive, splitting tensile and flexural strength increased 42%, 34%, and 28%, respectively. Based on SEM and XRD analyses, the author discerned that the binary combination of nano-Al₂O₃ and nano-TiO₂ improves the pore structure resulting in highly optimized mechanical properties. Nano-particles provide nucleation sites for the formation of additional C-S-H gel and control the growth of Ca(OH)₂ in the cement system. Therefore, the addition of a combination of nano-particles is more beneficial than the individual use of nano-particles.

construction & building technology,materials science, multidisciplinary,engineering, civil