Abstract:Vanadia-based catalysts have been widely used for catalyzing various reactions, including their long-standing application in the deNOx process. It has been commonly considered that various vanadium species dispersed on supports with a large surface area act as the catalytically active sites. However, the role of crystalline V2O5 in selective catalytic reduction of NOx with NH3 (NH3-SCR) remains unclear. In this study, a catalyst with low vanadia loading was synthesized, in which crystalline V2O5 was deposited on a TiO2 support that had been pretreated at a high temperature. Surprisingly, the catalyst, which had a large amount of crystalline V2O5, showed excellent low-temperature NH3-SCR activity. For the first time, crystalline V2O5 on low-vanadium-loading catalysts was found to be transformed to polymeric vanadyl species by the adsorption of NH3. The generated active polymeric vanadyl species played a crucial role in NH3-SCR, leading to remarkably enhanced catalytic performance at low temperatures. This new finding provides a fundamental understanding of the metal oxide-catalyzed chemical reaction and has important implications for the development and commercial applications of NH3-SCR catalysts.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/jacs.1c05354?goto=supporting-info">https://pubs.acs.org/doi/10.1021/jacs.1c05354</a>.XRD profiles, NH3-SCR activity, effect of SO2 on NOx conversion, NH3-TPD results, in situ DRIFTS, in situ Raman spectra, DFT calculation, and plot of the change in integral area of various Raman peaks (<a class="ext-link" href="/doi/suppl/10.1021/jacs.1c05354/suppl_file/ja1c05354_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Bulk tungsten-substituted vanadium oxide for low-temperature NOx removal in the presence of water

Selective Catalytic Removal of High Concentrations of NOx at Low Temperature

Active Vanadium(IV) Species Synthesized at Low-Temperature Facilitate Excellent Performance in Low-Temperature NOx-Catalytic Removal

Promotion Effect of Tungsten Oxide on SCR of NO with NH3 for the V2O5–WO3/Ti0.5Sn0.5O2 Catalyst: Experiments Combined with DFT Calculations

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

Substitution of WO3in V2O5/WO3–TiO2by Fe2O3for Selective Catalytic Reduction of NO with NH3

Adsorption-Induced Active Vanadium Species Facilitate Excellent Performance in Low-Temperature Catalytic NO x Abatement

Highly Efficient Mesoporous V2O5/WO3–TiO2 Catalyst for Selective Catalytic Reduction of NOx: Effect of the Valence of V on the Catalytic Performance

Vanadium Substitution As an Effective Way to Enhance the Redox Ability of Tungstophosphoric Acid and for Application of NH3-SCR

SO2 Promoted V2O5-MoO3/TiO2 Catalyst for NH3-SCR of NOx at Low Temperatures

Crystal Orientation-Dependent Activity of Tungsten-Based Catalysts for Selective Catalytic Reduction of NOx with NH3

Excellent low-temperature NH3-SCR of NO activity and resistance to H2O and SO2 over WaCeOx (a=0.06, 0.12, 0.18, 0.24) catalysts: Key role of acidity derived from tungsten addition

NOxRemoval over V2O5/WO3–TiO2Prepared by a Grinding Method: Influence of the Precursor on Vanadium Dispersion

Ammonium Ion Enhanced V2O5-WO3/TiO2 Catalysts for Selective Catalytic Reduction with Ammonia

New Insight into Alkali Resistance and Low Temperature Activation on Vanadia-Titania Catalysts for Selective Catalytic Reduction of NO

Selective catalytic reduction of NO with NH3 over novel iron–tungsten mixed oxide catalyst in a broad temperature range

V2O5-WO3/TiO2 Catalysts for Low Temperature NH3 SCR: Catalytic Activity and Characterization

Enhanced Hydrothermal Stability of a Manganese Metavanadate Catalyst Based on WO3–TiO2 for the Selective Catalytic Reduction of NOx with NH3

Alkali- and Sulfur-Resistant Tungsten-Based Catalysts for NOx Emissions Control.

Low Temperature Selective Catalytic Reduction of NO and NO2 with NH3 over Activated Carbon-Supported Vanadium Oxide Catalyst

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3