Abstract:Background: Fe80B20 amorphous alloys exhibit excellent soft magnetic properties, high abrasive resistance and outstanding corrosion resistance. In this work, Fe80B20 amorphous micro-fibers with HC of 3.33 Oe were firstly fabricated and the effects of annealing temperature on the structure and magnetic properties of the fibers were investigated. Methods: In this study, Fe80B20 amorphous fibers were prepared by the single roller melt-spinning method. The structures of as-spun and annealed fibers were investigated by X-ray diffractometer (XRD) (PANalytical X,Pert Power) using Cu Kα radiation. The morphology of the fibers was observed by scanning electron microscopy (SEM) (HITACHI-S4800). Differential scanning calorimetry (DSC) measurements of the fibers were performed on Mettler Toledo TGA/DSC1 device under N2 protection. Vibrating sample magnetometer (VSM, Versalab) was used to examine the magnetic properties of the fibers. The resonance behavior of the fibers was characterized by an impedance analyzer (Agilent 4294A) with a home-made copper coil. Results: The X-ray diffusion (XRD) patterns show that the fibers remain amorphous structure until the annealing temperature reaches 500°C. The differential scanning calorimetry (DSC) results show that the crystallization temperature of the fibers is 449°C. The crystallization activation energy is calculated to be 221 kJ/mol using Kissinger formula. The scanning electron microscopy (SEM) images show that a few dendrites appear at the fiber surface after annealing. The result indicates that the coercivity HC (//) and HC (⊥) slightly increases with increasing annealing temperature until 400°C, and then dramatically increases with further increasing annealing temperature which is due to significant increase in magneto-crystalline anisotropy and magneto-elastic anisotropy. The Q value firstly increases slightly when the annealing temperature rises from room temperature (RT) to 300°C, then decreases until 400°C. Eventually, the value of Q increases to ~2000 at annealing temperature of 500°C. Conclusions: In this study, Fe80B20 amorphous fibers with the diameter of 60 μm were prepared by the single roller melt-spinning method and annealed at 200°C, 300°C, 400°C, and 500°C, respectively. XRD results indicate that the fiber structure remains amorphous when the annealing temperature is below 400°C. α-Fe phase and Fe3B phase appear when the annealing temperature rises to 500°C, which is above the crystallization temperature of 449°C. The recrystallization activation energy is calculated to be 221 kJ/mol. The coercivity increases with increasing annealing temperature, which attributes to the increase of total anisotropy. All the as-spun and annealed fibers exhibit good resonance behavior for magnetostrictive sensors.

Crystal structure and magnetic properties study on barium hexaferrite of different average crystallite size

Effect of Annealing Temperature on Permeability and Giant Magneto-Impedance of Fe-based Amorphous Ribbon

Effect of Annealing on the Microstructure and Magnetic Properties of Fe-based Nanocomposite Materials

Effects of Crystal Structure, Morphology and Ion Diffusion During Annealing on Magnetic Properties of Hexagonal Barium Ferrite Films

Effects of Annealing Temperature on the Structures, Ferroelectric and Magnetic Properties of Aurivillius Bi5ti3feo15 Polycrystalline Films

Magnetization reversal and coercivity mechanism in ferromagnetic M-type hexaferrite by controlling phase evolution

Effect of annealing temperature on crystallographic texture, magnetic and microwave properties of barium ferrite thin films

Effects of boron content on the structure and magnetic properties of Fe81-xSi13BxMo2Cr1Cu1P2 nanocrystalline alloys

Study on quantitative Rietveld analysis of XRD patterns of different sizes of bismuth ferrite

Optimization of magnetic properties: Investigating the interaction of synthesis temperature, particle size, and monodomain formation in barium hexaferrite synthesized by the Pechini method

The Effects of Magnetic Field Annealing on the Magnetic Properties and Microstructure of Fe 80 Si 9 B 11 Amorphous Alloys

Improving the Magnetic Properties of Hydrothermally Synthesized Barium Ferrite

Influence of High-Temperature Annealing on Structural and Magnetic Properties of Crystalline Cobalt Ferrite Nanoparticles in the Single-Domain Regime

Effect of annealing temperature on morphology and magnetic properties of cobalt ferrite nanofibers

Effect of Al substitution on their structural and magnetic properties of Ba0.5Sr0.5Fe12O19 prepared via sol–gel auto-combustion method

Magnetic and structural characterization of nanosized BaCo_xZn_{2-x}Fe_{16}O_{27} hexaferrite in the vicinity of spin reorientation transition

Submicron Barium Hexaferrite Ceramics Manufactured by Low-Temperature Liquid-Phase Sintering of BaFe12O19 Nanoparticles

Structural, Dielectric and Magnetic Studies of Cobalt Ferrite Nanoparticles for Selected Annealing Temperatures

Effects of annealing on the structure and magnetic properties of Fe80B20 magnetostrictive fibers

Effect of Annealing Temperature on the Properties of BaFe12O19 Thin Films Deposited on GGG (111) Substrates by Pulsed Laser Deposition

Effect of annealing temperature on the properties of BaFe 12 O 19 thin films deposited on GGG (111) substrates by pulsed laser deposition