Abstract:In this work, the effects of Zn content (0–2 wt%) on microstructural evolution and mechanical properties of cast Mg–10Gd–3.5Er–0.5Zr alloys are studied. The results show that the as-cast Mg–10Gd–3.5Er– x Zn–0.5Zr alloys are mainly composed of Mg matrix and secondary (Mg, Zn) 3 (Gd, Er) phases distributed along grain boundaries. With the increase in Zn content, the volume fraction of secondary (Mg, Zn) 3 (Gd, Er) phases increases and the grains get refined. In the process of solid solution treatment, Zn addition can lead to the formation of long-period stacking ordered (LPSO) structures and the volume fraction of LPSO structures increases with Zn content. In addition, the Zn addition can reduce the vacancy formation energy and accelerate the diffusion rate of RE elements in Mg matrix. Because of the comprehensive effect of secondary phases and the accelerated diffusion rate, the base alloy and 2Zn alloy have less grain growth after solid solution treatment than that of the 0.5Zn alloy and 1Zn alloy. The precipitation process is also accelerated by enhanced diffusion rate. At room temperature (RT), the strengthening effect of β ʹ + β 1 precipitates is more effective than that of LPSO structures, so the peak-aged 0.5Zn alloy exhibits the most excellent mechanical performance at RT, with yield strength of 219 MPa, ultimate tensile strength 296 MPa and elongation of 6.4%. While LPSO structures have stronger strengthening effect at elevated temperature than that of β ʹ + β 1 precipitates, so the 1Zn alloy and 2Zn alloy have more stable mechanical performance than that of the base alloy and 0.5Zn alloy with the increase in tensile temperature.

Effect of the Addition of 0.5 wt % Zinc on the Microstructure and Properties of an Mg–2.3 wt % Y–0.7 wt % Zr–2.0 wt % Nd Alloy

Effects of Minor Y Addition on Microstructure and Mechanical Properties of Mg-Nd-Zn-Zr Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructural Characteristics and Mechanical Properties of Cast Mg–3Nd–3Gd–xZn–0.5Zr Alloys

Microstructures and Mechanical Properties of the Age Hardened Mg–4.2Y–2.5Nd–1Gd–0.6Zr (WE43) Microalloyed with Zn

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Microstructural Evolution and Mechanical Performance of Cast Mg-3Nd-0.2Zn-0.5Zr Alloy with Y Additions

Effect of Zn Addition on Microstructure and Mechanical Properties of Mg–9Gd–3Y–0.5Zr Alloy

Microstructure and Mechanical Properties of Mg-7Zn-3Al Alloy with Nd and Y Additions

Effect of Zn Concentration on the Microstructures and Mechanical Properties of Extruded Mg–7Y–4Gd–0.4Zr Alloys

Effect of Zn Addition on the Microstructure and Mechanical Properties of Cast Mg–10Gd–3.5Er– X Zn–0.5Zr Alloys

Effect of Zinc on Solidification and Aging Behaviour of Magnesium Alloys Containing Rare Earths

Chemical Composition Optimization of Gravity Cast Mg–yNd–xZn–Zr Alloy

Effect of Zn on the microstructure evolution of extruded Mg-3Nd (-Zn)-Zr (wt.%) alloys

Precipitation modification in cast Mg–1Nd–1Ce-Zr alloy by Zn addition

Effect of Zr on the microstructure, mechanical properties and corrosion resistance of Mg–10Gd–3Y magnesium alloy

Influence of Zn Content on Microstructure and Tensile Properties of Mg–Zn–Y–Nd Alloy

Effects of Nd on microstructures and properties at the elevated temperature of a Mg–0.3Zn–0.32Zr alloy

Improving mechanical properties of Mg–Zn-Nd-Zr alloy by low alloying with Yb and corresponding strengthening mechanisms

Effects of yttrium and zinc addition on the microstructure and mechanical properties of Mg–Y–Zn alloys