Abstract:In this work, SrBi4Ti4O15 (SBT) high-temperature piezoelectric ceramics with the addition of different oxides (Gd2O3, CeO2, MnO2 and Cr2O3) were fabricated by a conventional solid-state reaction route. The effects of oxide additives on the phase structures and electrical properties of the SBT ceramics were investigated. Firstly, X-ray diffraction analysis revealed that all these oxides-modified SBT ceramics prepared presented a single SrBi4Ti4O15 phase with orthorhombic symmetry and space group of Bb21m, the change in cell parameters indicated that these oxide additives had diffused into the crystalline lattice of SBT and formed solid solutions with it. The SBT ceramics with the addition of MnO2 achieved a high relative density of up to 97%. The temperature dependence of dielectric constant showed that the addition of Gd2O3 could increase the TC of SBT. At a low frequency of 100 Hz, those dielectric loss peaks appearing around 500 °C were attributed to the space-charge relaxation as an extrinsic dielectric response. The synergetic doping of CeO2 and Cr2O3 could reduce the space-charge-induced dielectric relaxation of SBT. The piezoelectricity measurement and electro-mechanical resonance analysis found that Cr2O3 can significantly enhance both d33 and kp of SBT, and produce a higher phase-angle maximum at resonance. Such an enhanced piezoelectricity was attributed to the further increased orthorhombic distortion after Ti4+ at B-site was substituted by Cr3+. Among these compositions, Sr0.92Gd0.053Bi4Ti4O15 + 0.2 wt% Cr2O3 (SGBT-Cr) presented the best electrical properties including TC = 555 °C, tan δ = 0.4%, kp = 6.35% and d33 = 28 pC/N, as well as a good thermally-stable piezoelectricity that the value of d33 was decreased by only 3.6% after being annealed at 500 °C for 4 h. Such advantages provided this material with potential applications in the high-stability piezoelectric sensors operated below 500 °C.

Enhanced piezoelectric properties of Ce-doped Bi3Ti1.5W0.5O9 high-temperature Aurivillius piezoceramics

Structural, dielectric, and piezoelectric properties of Ce-doped Bi7Ti4.2Ta0.3W0.5O21 intergrowth ferroelectric ceramics

Ultrahigh Temperature Bi3ti0.96sc0.02ta0.02nbo9-Based Piezoelectric Ceramics

High Performance Aurivillius-Type Bismuth Titanate Niobate (bi3tinbo9) Piezoelectric Ceramics for High Temperature Applications

High Piezoelectricity and Thermal Stability of Ce-doped CaBi2Nb2O9-based High-Temperature Ceramics

Effect of W/Cr co-doping on electrical properties of Ca0.94Ce0.06Bi4Ti4O15 high-temperature piezoceramics

The impact of co-doping Ce, W, and Mn on the microstructure and piezoelectric performance of high-temperature piezoelectric ceramics based on CaBi2Nb2O9

Facile Preparation and Performance of Novel High-Tc Xbi(ni1/2ti1/2)o3-(1-x)pb(zr1/2ti1/2)o3 Piezoceramics

Enhancing Electrical Properties of High-Curie Temperature Piezoelectric Ceramics BNT-PZT and Their Mechanism

Simultaneously Achieved High Piezoelectricity and Resistivity in CaBi2Nb2O9-based Ceramics with High Curie Temperature

Simultaneously Achieved High Piezoelectricity and High Resistivity in Na0.5Bi4.5Ti4O15-Based Ceramics with High Curie Temperature

Impact of crystal structure and defect on the electric properties in (LiCeY)-doped CaBi2Nb2O9-based high-temperature piezoceramics

Effect of (K0.5Ce0.5) complex on the electrical properties of lead‐free Bi4Ti2.86W0.14O12 high‐temperature piezoelectric ceramics

Effects of Oxide Additives on the Phase Structures and Electrical Properties of SrBi4Ti4O15 High-Temperature Piezoelectric Ceramics

Enhanced high-temperature piezoelectric properties of Bi(Zn0.5Ti0.5)O3-modified BiFeO3–BaTiO3 ceramics

Enhanced ferroelectric, piezoelectric and dielectric properties of (1-<i>x</i>) CaBi<sub>2</sub>Nb<sub>2</sub>O<sub>9</sub>-<i>x</i>BaZr<sub>0.2</sub>Ti <sub>0.8</sub>O<sub>3</sub> high-temperature piezoelectric composite ceramics

Ce and W co-doped CaBi2Nb2O9 with enhanced piezoelectric constant and electrical resistivity at high temperature

Lead-Free BiFeO3-BaTiO3 Ceramics with High Curie Temperature: Fine Compositional Tuning Across the Phase Boundary for High Piezoelectric Charge and Strain Coefficients.

Enhanced Piezoelectric Activity with Good Thermal Stability and Improved Electrical Resistivity in Ta–Mn Co-Doped CaBi4Ti4O15 High-Temperature Piezoceramics

Enhanced electrical properties in Ce/Mo co-substituted CaBi 2 Nb 2 O 9 high-temperature piezoelectric ceramic

Electromechanical Properties of A-Site (Lice)-Modified Sodium Bismuth Titanate (na0.5bi4.5ti4o15) Piezoelectric Ceramics at Elevated Temperature