Structures and impact strength variation of chemically crosslinked high-density polyethylene: effect of crosslinking density

Yueqing Ren,Xiaojie Sun,Lanlan Chen,Yafei Li,Miaomiao Sun,Xuelei Duan,Wenbin Liang

DOI: https://doi.org/10.1039/d0ra10365a

IF: 4.036

2021-01-01

RSC Advances

Abstract:Crosslinking significantly improves the toughness and impact strength of HDPE and extends its application, especially at low temperature.

chemistry, multidisciplinary

What problem does this paper attempt to address?

The effect of chemical crosslinking on the properties of Rotomolded high density polyethylene

Hibal Ahmad,Ehsan Rostami‐Tapeh‐Esmaeil,Denis Rodrigue

DOI: https://doi.org/10.1002/app.54744

IF: 3

2023-09-30

Journal of Applied Polymer Science

Abstract:The level of polyethylene crosslinking can be determined via different properties. In this study, high density polyethylene (HDPE) was combined with dicumyl peroxide (DCP) to produce crosslinked parts via rotational molding. The effect of DCP content (0.1–2.5 phr) on the crosslinking degree was investigated to determine its effect on the chemical, mechanical, physical, and thermal properties of HDPE. The gel content and crosslink density was found to increase with DCP content. These trends led to a reduction in the degree of crystallinity, melting, and crystallization temperature. Thermogravimetric analysis (TGA) showed that crosslinked HDPE (xHDPE) has higher thermal stability than the neat matrix in both air and nitrogen atmosphere. In addition, a direct relationship was observed between improved thermal resistance and higher impact strength. Finally, relationships between the tensile properties of xHDPE and the degree of crystallinity were observed, which were all controlled by the level of crosslinking. These results have the potential to advance the manufacturing of high performance materials suitable for a wide range of applications such as automotive parts, agricultural products, chemical storage tanks, large waste containers, and fuel tanks in general.

polymer science
Influence of Crosslink Density on Electrical Performance and Rheological Properties of Crosslinked Polyethylene

Linting Di,Chenyuan Qin,Wenying Wang,Anping Huang,Fuqing Wei,Huifang Xu,Shiyuan Yang

DOI: https://doi.org/10.3390/polym16050676

IF: 5

2024-03-02

Polymers

Abstract:To investigate the influence of the crosslinked polyethylene (XLPE) structure on electrical performance, various analytical methods were employed to study polyethylene structures with different degrees of crosslinking. Dynamic rheological analysis was conducted to determine material shear viscosity, dynamic viscosity, storage modulus (G′), loss modulus (G′′), and other rheological parameters. Additionally, the electrical performance of the material was analyzed by studying the phenomenon of space charge accumulation under direct current voltage. The results indicate that with an increasing mass fraction of the crosslinking agent, the crosslink density of crosslinked polyethylene initially increases and then decreases. When the dicumyl peroxide (DCP) content exceeds 1.0 wt.%, there is an accumulation of like-polarity space charges. The best rheological processing performance of crosslinked polyethylene is observed when the DCP content is in the range of 1.0–1.5 wt.%.

polymer science
New Insight on Improving Electrical Strength and Toughness of Polyethylene Blends: Turning Point of Supramolecular Structure

Lunzhi Li,Lisheng Zhong,Kai Zhang,Jinghui Gao,Man Xu,Yu Wang

DOI: https://doi.org/10.1063/1.5053416

IF: 1.697

2018-01-01

AIP Advances

Abstract:We report an effective approach on improving the electrical strength and mechanical impact toughness in polyethylene blends by locating the composition on a submicroscopic supramolecular structure turning point. The designed linear low density polyethylene (LLDPE)-high density polyethylene (HDPE) blends exhibit the enhanced electrical breakdown strength and toughness with the optimal value of E0=95.48kV/mm and G=54.67 kJ·m-2 respectively, which is around 6% and 18% higher than pure LLDPE. The scanning electron microscopic (SEM) investigation and X-ray diffraction (XRD) study show no obvious variation in mesoscopic and microscopic structure with the change of HDPE content. Further differential scanning calorimetric (DSC) study using successive self-nucleation/annealing (SSA) method reveals that the turning point with optimal performance corresponds with a peculiar supramolecular structure with a high density of tie molecules, which enhances the toughness and the electromechanical breakdown strength. Our work provides a new insight on improving electrical strength and toughness for dielectric polymers, and may aid to enhance the electric insulation performance for dielectric materials in power equipment.
Enhanced Strength and Foamability of High-Density Polyethylene Prepared by Pressure-Induced Flow and Low-Temperature Crosslinking

Tairong Kuang,Feng Chen,Dajiong Fu,Lingqian Chang,Xiangfang Peng,Ly James Lee

DOI: https://doi.org/10.1039/c6ra05238j

IF: 4.036

2016-01-01

RSC Advances

Abstract:We report a high-performance high-density polyethylene (HDPE) with significantly enhanced mechanical strength by means of pressure-induced flow (PIF) and low-temperature crosslinking treatment. The tensile and flexural strengths increased from 23.5 and 36.2 MPa, up to 74.8 and 78.6 MPa, respectively. This was achieved by the elongated and flattened 'brick-and-mud' like crystal structure of HDPE occurred during PIF, and an adequate crosslinking network that was formed in the amorphous region beneath the melting point. Furthermore, high strength foams of this material could also be produced under super-critical CO2 batch foaming in solid-state.
Influence of Crosslinking on Crystallization, Rheological, and Mechanical Behaviors of High Density Polyethylene/ethylene‐vinyl Acetate Copolymer Blends

Xiaohu Zhang,Hongmei Yang,Yihu Song,Qiang Zheng

DOI: https://doi.org/10.1002/pen.23843

2014-01-01

Abstract:High density polyethylene (HDPE)/ethylene‐vinyl acetate copolymer (EVA) blends with selective crosslinking the EVA phase were prepared and the crystallization, rheological, and mechanical behaviors were studied. Selective crosslinking of EVA component could greatly improve both tensile and impact strengths of the HDPE‐rich blends and influence melting enthalpy at different annealing temperature in successive self‐nucleation and annealing procedure. Dynamic mechanical analysis reveals that glass transition temperatures of both the HDPE and EVA components are lowered upon blending and are raised upon crosslinking. The uncrosslinked HDPE/EVA blends are unstable in the melt and show increment in storage modulus (G′) and decay in loss tangent (tanδ) with annealing time associated with phase coarsening. However, morphology of selectively crosslinked blends in the melt state is highly unstable, characterized by a fast migration of uncrosslinked HDPE component out of the crosslinked EVA phase to the surface resulting in a rapid decay in G′ and an increment in tanδ at the early stage of annealing. POLYM. ENG. SCI., 54:2848–2858, 2014. © 2014 Society of Plastics Engineers
EFFECTS OF CROSSLINKING AGENTS ON RADIATION CROSSLINKING OF LLDPE/EPDM BLENDS

朱光明,徐前永,施永勤

DOI: https://doi.org/10.3969/j.issn.1000-3436.2002.01.012

2002-01-01

Journal of Radiation Research and Radiation Processing

Abstract:The effects of 3 additives (sulfur, trimethylolpropane triacrylate (TMPTA) and petaerythritol tetraacrylate (PETA) on radiation cross-linking of LLDPE-EPDM are investigated in this paper. The gel percentage content, mechanical properties and heat age resistances of the blends with various compositions and radiation dosage have been studied. It can be concluded that all the 3 additives are helpful to the radiation cross-linking of LLDPE-EPDM blends and could approve its properties, but sulfur is the best. Based on the above, the blended materials with tensile strength and elongation above 20 MPa, 500% respectively have been made by LLDPE 100, EPDM 50-100, S 0.5-2 parts and other additives 30-40 parts. These materials also have the characteristics of excellent heat aging, weather resistance, low temperature flexibility and toughness. They can be used for the outer jacketing of wire or cable, pliability and strong heat shrinking products.
The effects of crosslink density on thermo-mechanical properties of shape-memory hydro-epoxy resin

Kun Wei,Guangming Zhu,Yusheng Tang,Tingting Liu,Jianqiang Xie

DOI: https://doi.org/10.1557/jmr.2013.277

IF: 2.7

2013-01-01

Journal of Materials Research

Abstract:The objective of this work is to reveal the relationship between the molecular structure and shape-memory property of a hydro-epoxy resin system. The system is prepared using hydro-epoxy, menthane diamine (MDA), and poly(propylene glycol) diglycidyl ether (PPGDGE) with different molecular weights. By keeping the PPGDGE content constant, the crosslink density of the shape-memory hydro-epoxy resin system can be changed by varying the molecular weight of PPGDGE. The results indicate that the glass transition temperature ( T g ) and rubber modulus ( E r ) decrease as the crosslink density decreases. The crosslink density has little influence on shape recovery ratio ( R r ). Full recovery can be observed after only several minutes when the temperature is equal to or above T g . However, the crosslink density has a profound effect on the shape fixity ratio ( R f ). If the crosslink density is too low, the shape fixity ratio of shape-memory hydro-epoxy resin would not reach 100%.
INFLUENCE OF CROSSLINKING ON PHYSICAL PROPERTIES OF LOW DENSITY POLYETHYLENE

Xiao-hu Zhang,Hong-mei Yang,Yi-hu Song,Qiang Zheng

DOI: https://doi.org/10.1007/s10118-012-1194-3

2012-01-01

Chinese Journal of Polymer Science

Abstract:Influence of crosslinking on physical properties of low density polyethylene was studied.The results indicated that, at low degrees of crosslinking, the network hardly affects the crystallinity, elastic modulus (E) and yielding stress while it improves the tensile strength and strain at break simultaneously. Tensile strength reaches a maximum of about 24 MPa at 1.5 phr dicumyl peroxide (DCP) then decreases to a constant value of about 18 MPa due to decrease of crystallinity. E reaches its maximum at 0.5 phr DCP corresponding to gel fraction of about 75% without marked change in crystallinity. The crosslinked polyethylene exhibits two yielding processes, and both yielding stresses approximately linearly depend on crystallinity.
Crystallization and Fracture Behaviors of High‐density Polyethylene/linear Low‐density Polyethylene Blends: the Influence of Short‐chain Branching

Guanghao Shen,Hongwang Shen,Banghu Xie,Wei Yang,Mingbo Yang

DOI: https://doi.org/10.1002/app.38937

IF: 3

2013-01-01

Journal of Applied Polymer Science

Abstract:Two commercial polyethylene samples, linear high-density polyethylene (HDPE) and branched linear low-density polyethylene with almost the same molecular weight distribution but different contents of short-chain branching (SCB) were melt blended based on the consideration of practical application. Dynamic rheology analysis indicated good compatibility of all the blends with different compositions. Common differential scanning calorimeter (DSC) tests and successive self-nucleation and annealing (SSA) treatment showed several interesting phenomena. First, without consideration of the effect of molecular weight and molecular weight distribution impact, co-crystallization occurred at all ratios even the two components had a considerable difference in SCB distribution. Second, in SSA curves the area of the first two melting peaks, i.e., the amount of the thick lamellas of the two components showed an obvious positive deviation with the increase of HDPE content owing to the crystal perfection improved by the co-crystallization. Essential Work of Fracture tests proved the co-crystallization effects had a positive effect on the improvement of the resistance to crack propagation. (c) 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013
Effects of Fiber Characteristics on Tensile and Impact Properties of Long Fiber Reinforced High-Density Polyethylene

Lijuan Jiang,Xin Wang,Yinzhi Zhou

DOI: https://doi.org/10.1002/pc.28537

IF: 5.2

2024-01-01

Polymer Composites

Abstract:Due to the requirements of high stiffness and impact strength of HDPE pipes, in this article, long fiber reinforced HDPE were developed and the effects of fiber length, volume fraction, types, and matrix/fiber interface on the mechanical properties were investigated. Tensile properties, notched impact strength, as well as microstructures were tested. The results showed that fibers increased the tensile strength, modulus, and impact strength, but decreased their plastic deformation. Larger fiber fraction indicates more fibers are involved in load bearing, but easy agglomeration. With ascending fiber length, tensile, and impact strength first increased and then decreased, whereas tensile modulus first increased and then maintained an almost constant value. Carbon fibers showed no advantages over glass fibers and basalt fibers in reinforcing HDPE due to the relatively poor interface bonding strength. Interface modification with KH550 improved the mechanical performance of composites, but the enhancement was limited. More effective methods should be developed for better performance.
Effects of Matrix Molecular Weight on Structure and Reinforcement of High Density Polyethylene/Mica Composites

Li Chen,Yu-fang Xiang,Ke Wang,Qin Zhang,Rong-ni Du,Qiang Fu

DOI: https://doi.org/10.1007/s10118-011-1035-9

2011-01-01

Abstract:Three types of high-density polyethylene (HDPE) with different molecular weights (high, medium and low) were adopted to evaluate the influence of matrix molecular weight on the structure-property relation of injection-molded HDPE/mica composites through a combination of SEM, 2d-WAXS, DSC, DMA and tensile testing. Various structural factors including orientation, filler dispersion, interfacial interaction between HDPE and mica, etc., which can impact the macroscopic mechanics, were compared in detail among the three HDPE/mica composites. The transcrystallization of HDPE on the mica surface was observed and it exhibited strong matrix molecular weight dependence. Obvious transcrystalline structure was found in the composite with low molecular weight HDPE, whereas it was hard to be detected in the composites with increased HDPE molecular weight. The best reinforcement effect in the composite with low molecular weight HDPE can be understood as mainly due to substantially improved interfacial adhesion between matrix and mica filler, which arises from the transcrystallization mechanism.
Influence of Molecular Weight on Impact Fracture Behavior of Injection Molded High Density Polyethylene: Scanning Electron Micrograph Observations

Bin Li,Guan Gong,Bang-Hu Xie,Wei Yang,Ming-Bo Yang

DOI: https://doi.org/10.1002/app.28143

IF: 3

2008-01-01

Journal of Applied Polymer Science

Abstract:A group of high density polyethylene with different molecular weight was prepared by melt blending two kinds of HDPE with weight average molecular weight of 3.2 X 10(5) g/mol and 7.2 X 10(5) g/mol, respectively. The fracture behavior of injection molded specimens of these samples was investigated by Izod impact test and scanning electron microscopy. The results show that the variations of impact toughness of injection molded HDPE could be reflected directly by the evolution of morphology of fracture surface as molecular weight increases. Higher molecular weight led to higher impact toughness, due to both thickened oriented shear zone which could enhance the crack resistance and depressed two types of fracture behavior (tearing-brittle fracture and heat softening/melting fracture) with low energy consumption. Fracture behavior in different position of injection molded HDPE shows different molecular weight dependence. The impact toughness at far-gate-end increases with increasing molecular weight, while the impact toughness at near-gate-end, especially for the blends, almost keeps constant within a certain range of molecular weight. (c) 2008 Wiley Periodicals, Inc.
Morphology evolution and mechanical property enhancement of linear low‐density polyethylene by adding disentangled ultrahigh molecular weight polyethylene

Yu Zhang,Yutao Di,Chunlin Ye,Letian Zhang,Xin Tang,Baoqiang Shu,Xiang Yan,Wei Li,Jingdai Wang,Yongrong Yang

DOI: https://doi.org/10.1002/pat.5577

IF: 3.348

2021-12-14

Polymers for Advanced Technologies

Abstract:Abstract Ultra‐high molecular weight polyethylene (UHMWPE) and linear low‐density polyethylene (LLDPE) with different ratios were melt‐blended in an internal mixer. Results of rheological tests and scanning electron microscopy indicate that the blends are well miscible in the range of small addition amount of UHMWPE. The content of UHMWPE is suggested to be less than 5.0 wt%, to guarantee good compatibility of biphasic blends. Differential scanning calorimetry studies indicate that co‐crystallization occurs between UHMWPE and LLDPE. The crystallinity increases with the increase of UHMWPE as a nucleating agent. As a result, an improvement in mechanical properties is achieved. When the addition amount of UHMWPE is 5.0 wt%, the impact strength, breaking elongation, Young's modulus, and tensile strength are significantly increased by 27%, 25%, 75%, and 21% respectively.

polymer science
Simultaneously enhancing strength and toughness for impact polypropylene copolymers by regulating the dispersed phase with high density polyethylene

biwei qiu,feng chen,yonggang shangguan,lina zhang,yu lin,qiang zheng

DOI: https://doi.org/10.1039/c4ra10682b

IF: 4.036

2014-01-01

RSC Advances

Abstract:By introducing high density polyethylene (HDPE) into the dispersed phase of impact polypropylene copolymers (IPCs), the morphologies of IPC/HDPE blends were regularly tailored and consequently the tensile and impact properties were simultaneously improved. Morphological observations showed a series of multilayered core-shell dispersed particles when the content of HDPE was less than 40%, while the continuous network structure was observed beyond 40%. With an increase in the content of HDPE, the size of the core increased and the number of dispersed particles with incomplete encapsulated polyethylene (PE) cores rose. More valid 'bridges' made up of segmented ethylene-propylene copolymer (sEbP) appeared and connected the PE core and polypropylene (PP) matrix. Meanwhile, co-crystallization occurred in the core phase, between long ethylene chain segments of the joined HDPE and sEbP in multi-component IPCs. The increased HDPE in blends reduced defective co-crystals, and in turn led to a thicker average lamellar thickness and thinner amorphous thickness of PE. Partial inserted ethylene-propylene random sequences are constrained by narrowed PE amorphous layers. Hence, the connection between the PP matrix and the dispersed phase was strengthened by co-crystals, 'bridges' and restriction effects. The tensile strength of the blends was slightly enhanced with an increase in HDPE, while the greatly improved toughness was achieved at a HDPE content of 30 wt% and kept constant with more HDPE. Thus, the interactions rather than core-shell phase morphology are regarded as the predominate factor for the excellent properties.
Effects of Polymerization and Crosslinking Technologies on the Crystallization Behaviors and Gel Network of Crosslinked Polyethylene

Jing-Gang Gai,Shi-Peng Zhu,Jian Kang,Ya Cao,Ming Xiang

DOI: https://doi.org/10.1080/00222348.2011.629900

2012-01-01

Abstract:In the present study, we investigated the influences of polymerization and crosslinking technologies on the branched-chain structures, crystallization behaviors, and gel networks of two types of low-density polyethylenes, LDPE1 and LDPE2, polymerized under different polymerization conditions in commercial large-capacity production lines. High temperature 13C NMR analysis suggests that the molar contents of both long-chain branches and short-chain branches of LDPE2 were markedly higher than those of LDPE1 due to a higher polymerization temperature for LDPE2. The high content of chain branches of LDPE2 leads to its relatively higher storage modulus, entanglement density, and gel content, as indicated by dynamic mechanical analysis. In addition, when the crosslinking temperature reached 180°C, the LDPE2 crosslinked with 2 wt% dicumylperoxide (XLPE2-D2) displayed a relatively wider processing time window and a faster crosslinking rate than XLPE1-D2. Successive self-nucleation and annealing fractionation indicated that increasing the concentration of dicumylperoxide can improve the crosslinking degree, but resulted in lower crystallinity and thinner lamellar crystals.
Effect of Different Morphologies on Slow Crack Growth of High-Density Polyethylene

Yuxi Pan,Xueqin Gao,Zhongwu Wang,Jun Lei,ZhongMing Li,KaiZhi Shen

DOI: https://doi.org/10.1039/c5ra00918a

IF: 4.036

2015-01-01

RSC Advances

Abstract:We made different morphologies of HDPE using OSIM to increase the resistance to SCG.
High Speed Injection Molding of High Density Polyethylene — Effects of Injection Speed on Structure and Properties

Kun Jiang,Fei-long Yu,Run Su,Jing-hui Yang,Tian-nan Zhou,Jian Gao,Hua Deng,Ke Wang,Qin Zhang,Feng Chen,Qiang Fu

DOI: https://doi.org/10.1007/s10118-011-1049-3

2011-01-01

Abstract:>Thin wall samples of high density polyethylene(HDPE)were prepared via injection molding with different injection speeds ranging from 100 mm/s to 1200 mm/s.A significant decrease in the tensile strength and Young’s modulus was observed with increasing injection speed.In order to investigate the mechanism behind this decrease,the orientation, molecular weight,molecular weight distribution,melt flow rate,crystallinity and crystal morphology of HDPE were characterized using two-dimensional wide-angle X-ray diffraction(2D-WAXD),gel permeation chromatography(GPC), capillary rheometry and differential scanning calorimetry(DSC),respectively.It is demonstrated that the orientation, molecular weight,molecular weight distribution,melt flow rate and crystallinity have no obvious change with increasing injection speed.Nevertheless,the content of extended chain crystals or large folded chain crystals was found to decrease with increasing injection speed.Therefore,it is concluded that the decrease in tensile properties is mainly contributed by the reduced content of extended chain crystals or large folded chain crystals.This study provides industry with valuable information for the application of high speed injection molding.
Influence of Cross-Linking on Fracture Behavior of co-Polypropylene

HUANG Hui-juan,XIE Bang-hu,YANG Wei,YANG Ming-bo

2010-01-01

Abstract:The cross linking modification of polypropylenes was investigated via increasing the amount of modifiers,under constant rate of initiator (DCP) and auxiliary cross-linking agent (DVB). The fracture behaviors as well as the influence of the structure of polypropylenes on fracture performances were intensively studied using the method of essential work of fracture (EWF). It is concluded that the chain structure and fracture behaviors are significantly influenced by the different amount of modifiers. The addition of modifiers is in favor of the formation of cross-linking structure and limites the slip between molecular chains or grains subsequently. With lower amount of cross-linking structure,we decreases with the increased dosage of modifier,while βwp increases with it. However,the trends of both we and βwp are just on the contrary within higher amount of cross-linking structure.
Photocross‐linking of Low‐density Polyethylene. II. Structure and Morphology

BJ QU,B RANBY

DOI: https://doi.org/10.1002/app.1993.070480413

IF: 3

1993-01-01

Journal of Applied Polymer Science

Abstract:Morphological structure and other properties of polyethylene photocross-linked in the melt (XLPE) have been studied by wide-angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), density, and swelling measurements. The WAXD measurements show that the crystallinity of polyethylene decreases with increasing gel content in the XLPE samples and that the regularity and the size of crystals are affected by photocross-linking. DSC data confirm that photocross-linking occurs preferentially in the amorphous and interfacial regions and causes depression of the melting point and decreases the heat of fusion. The density of XLPE apparently decreases with increasing gel content, which is due to decreased crystallinity and lattice expansion. The cross-link density determined by the swelling measurements and evaluated using the Flory-Rehner equation correlates well with the changes in crystallinity and melting point.
Model Simulation and Rheological Research on Crosslinking Behavior of Polyethylene Resin

Xuelian Chen,Qigu Huang

DOI: https://doi.org/10.3390/gels10010035

IF: 4.6

2024-01-01

Gels

Abstract:The crosslinking behavior of polyethylene (PE) determines its exceptional performance and application. In this study, we investigated the crosslinking behaviors of different PE resins through model simulation and rheological methods. Specifically, the mathematical equation of "S" model was established for PE resin. According to this equation, the optimal maximum gel content for high-density polyethylene (HDPE) was found to be around 85%. Moreover, the maximum crosslinking degrees for different PE resins depended largely on their density and molecular weight. The melt viscosities before crosslinking in PE resins were highly influenced by their melt index. The higher melt indexes resulted in the lower storage moduli, improving melt processability during processing. In addition, the crosslinking rates of PE resins were strongly influenced by peroxide concentration, independent of PE resin structures. For high molecular weight and low-density PE resins, they exhibited decreased ti values, increased A0 values, and decreased k6 values. However, there were no noticeable variations in the values of k2 and phi among different PE resins. All simulated modeling outcomes showed remarkable consistency with the experimental rheological data. These findings are of strong significance in the industrial manufacture of PE resin.

polymer science

Structures and impact strength variation of chemically crosslinked high-density polyethylene: effect of crosslinking density

The effect of chemical crosslinking on the properties of Rotomolded high density polyethylene

Influence of Crosslink Density on Electrical Performance and Rheological Properties of Crosslinked Polyethylene

New Insight on Improving Electrical Strength and Toughness of Polyethylene Blends: Turning Point of Supramolecular Structure

Enhanced Strength and Foamability of High-Density Polyethylene Prepared by Pressure-Induced Flow and Low-Temperature Crosslinking

Influence of Crosslinking on Crystallization, Rheological, and Mechanical Behaviors of High Density Polyethylene/ethylene‐vinyl Acetate Copolymer Blends

EFFECTS OF CROSSLINKING AGENTS ON RADIATION CROSSLINKING OF LLDPE/EPDM BLENDS

The effects of crosslink density on thermo-mechanical properties of shape-memory hydro-epoxy resin

INFLUENCE OF CROSSLINKING ON PHYSICAL PROPERTIES OF LOW DENSITY POLYETHYLENE

Crystallization and Fracture Behaviors of High‐density Polyethylene/linear Low‐density Polyethylene Blends: the Influence of Short‐chain Branching

Effects of Fiber Characteristics on Tensile and Impact Properties of Long Fiber Reinforced High-Density Polyethylene

Effects of Matrix Molecular Weight on Structure and Reinforcement of High Density Polyethylene/Mica Composites

Influence of Molecular Weight on Impact Fracture Behavior of Injection Molded High Density Polyethylene: Scanning Electron Micrograph Observations

Morphology evolution and mechanical property enhancement of linear low‐density polyethylene by adding disentangled ultrahigh molecular weight polyethylene

Simultaneously enhancing strength and toughness for impact polypropylene copolymers by regulating the dispersed phase with high density polyethylene

Effects of Polymerization and Crosslinking Technologies on the Crystallization Behaviors and Gel Network of Crosslinked Polyethylene

Effect of Different Morphologies on Slow Crack Growth of High-Density Polyethylene

High Speed Injection Molding of High Density Polyethylene — Effects of Injection Speed on Structure and Properties

Influence of Cross-Linking on Fracture Behavior of co-Polypropylene

Photocross‐linking of Low‐density Polyethylene. II. Structure and Morphology

Model Simulation and Rheological Research on Crosslinking Behavior of Polyethylene Resin