Abstract:Vanadium dioxide (VO2) is considered to be one of the most competitive thermochromic materials, due to its semiconductor-metal phase transition characteristics. And the doping of tungsten (W) into the lattice of VO2 can significantly reduce the phase transition temperature to near room temperature. However, the reduction efficiency dependent on doping amount is quite different in previous reports. In this work, we proposed an in-situ stirring assisted hydrothermal to synthesize W-doped VO2 nanorods with improved doping efficiency. The effects of in-situ stirring during the hydrothermal synthesis on phase composition, sample morphology, and phase-transition temperature of VO2 with different W doping amounts were studied systematically. The phase transition temperature reduction efficiency of W-doped VO2 prepared by hydrothermal synthesis without in-situ stirring was at % W. By contrast, the phase transition temperature of W-doped VO2 prepared by in-situ stirring hydrothermal synthesis was depressed as much as 24.55 degrees C/at % W when W/V ranged in 0.75-2.0 at %. Further research found that the phase transition temperature of W-doped VO2 (M) could be simply tuned by changing the in-situ stirring time. Then, the 1 at% W-doped VO2 (M) (with phase transition temperature of around 41.5 degrees C) nanorods and acrylic resin were mixed to prepare VO2 composite film. It exhibited suitable infrared transmission (>60%) and excellent mid-infrared transmission switching performance (23.77%). This work proposed an in-situ stirring hydrothermal method for high efficiency synthesis of W-doped VO2 (M) and provided significant insights for its application in thermochromic windows. (C) 2020 Elsevier B.V. All rights reserved.

Accelerated microwave-assisted synthesis and in situ X-ray scattering of tungsten-substituted vanadium dioxide (V1−xWxO2)

Local structure elucidation of tungsten-substituted vanadium dioxide (V[Formula: see text]W[Formula: see text]O[Formula: see text])

Structural phase transition of tungsten-doped vanadium dioxide nanopowders prepared by thermolysis

Hydrothermal synthesis and characterization of W-doped VO_2 nano-particles

Preparation and Thermochromic Property of Tungsten-Doped Vanadium Dioxide Particles

Preparation, Characterization and Properties of Thermochromic Tungsten-Doped Vanadium Dioxide by Thermal Reduction and Annealing

Tungsten-doped vanadium dioxide thin film synthesis by alternate layer-by-layer growth and post-deposition annealing

Stabilization of the VO2(M2) Phase and Change in Lattice Parameters at the Phase Transition Temperature of WXV1- XO2 Thin Films

Effect of W-Mo Doping on the Phase Transition Temperature of VO2 Synthesized by Hydrothermal Microwave Method

Depressed transition temperature of W(x)V(1-x)O2: mechanistic insights from the X-ray absorption fine structure (XAFS) spectroscopy

Microstructures and thermochromic properties of tungsten doped vanadium oxide film prepared by using VOX–W–VOX sandwich structure

Phase, Microstructure, Thermochromic, and Thermophysical Analyses of Hydrothermally Synthesized W-Doped VO2 Nanopowder

Depressed Transition Temperature of Wxv1-Xo2: Mechanistic Insights from the X-Ray Absorption Fine Structure (xafs) Spectroscopy

One-Step Hydrothermal Conversion of Vo2(B) into W-Doped Vo2(M) and Its Phase Transition and Optical Switching Properties

Optical, Electrical, Structural, and Thermo-Mechanical Properties of Undoped and Tungsten-Doped Vanadium Dioxide Thin Films

Doping-driven Electronic and Lattice Dynamics in the Phase-Change Material Vanadium Dioxide

Preparation Of Tungsten-Doped Vo2 (M) Nanoparticles Through Sol-Gel Method And Hydrothermal Synthesis

Synthesis and Thermal Stability of W-doped VO2 Nanocrystals

In-situ Stirring Assisted Hydrothermal Synthesis of W-doped VO2 (M) Nanorods with Improved Doping Efficiency and Mid-Infrared Switching Property

Synthesis of Tungsten-Doped Vanadium Dioxide Using a Modified Polyol Method Involving 1-Dodecanol

Synthesis, characterization, and thermodynamic parameters of vanadium dioxide