Abstract:Tungsten fiber-reinforced tungsten composite (Wf/W) material is considered a plasma-facing material (PFM) with good application prospects. Commercial tungsten wire (fiber) prepared through forging and drawing processes has excellent mechanical properties, as well as a very high recrystallization temperature due to the unique texture of it grain structure. Commercial tungsten fiber is the most proper reinforcement for Wf/W. The change in the properties of tungsten fiber because of neutron irradiation makes it inevitable for Wf/W to be used as PFMs. However, there is very little research on the change in the properties of tungsten fiber caused by neutron irradiation. In this work, we used heavy ion irradiation to simulate the displacement damage generated by neutron irradiation to explore the alteration of the properties of a commercial tungsten fiber caused by neutron irradiation. The investigated subject was tungsten fiber with a diameter of 300 μm. The irradiation source was 7.5 MeV Au2+, which generated a maximum displacement damage of 60 dpa at a depth of 400 nm, and the irradiation influenced depth was 1000 nm. Because of the irradiation, significant lattice distortion occurred within the tungsten fiber, resulting in the transition from (110) texture to (100) texture at the fiber’s cross-section. The results of the Schmidt factor and Taylor factor analysis indicate a decrease in the plasticity of the tungsten fiber after irradiation, but it did not completely lose its plasticity. The results of the nanoindentation test confirmed the radiation hardening. After irradiation, the hardness of the tungsten fiber increased by approximately 0.33 GPa, but this increase was relatively small compared to other tungsten-based materials. This indicates that commercial tungsten fiber is a low-cost and highly reliable reinforcement material for Wf/W composite materials.

Recent progress of radiation response in nanostructured tungsten for nuclear application

The Microstructural and Hardness Changes of Tungsten Fiber after Au2+ Irradiation

Recent Progress on Interfaces in Nanomaterials for Nuclear Radiation Resistance

Interaction of radiation-induced defects with tungsten grain boundaries at across scales: a short review

Radiation Damage in Nanostructured Materials

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

A Brief Review of the Impact of Neutron Irradiation Damage in Tungsten and Its Alloys

Progress in Irradiation Damage of Tungsten and Tungsten Alloys Under Different Irradiation Particles

Radiation Effects in Novel Nuclear Materials

Research Progress in Damage of Tungsten and Tungsten-base Materials for Nuclear Fusion Device

Research and development of nanocrystalline W/W-based materials: novel preparation approaches, formation mechanisms, and unprecedented excellent properties

Research Progress on the Interface Design and Interface Response of Irradiation Resistant Metal-Based Nanostructured Materials

Review of Irradiation Damage Behavior of Tungsten Exposed to Plasma in Nuclear Fusion

A Review on the Radiation Response of Nanoporous Metallic Materials

Combinatorial discovery of irradiation damage tolerant nano-structured W-based alloys

Molecular Dynamics Simulation of Nanoporous Tungsten

Development of irradiation tolerant tungsten alloys for high temperature nuclear applications

Neutron Irradiation-Induced Recrystallization Simulation for Tungsten in Nuclear Fusion Device

Enhancing resistance to radiation hardening and radiation thermal conductivity degradation by tungsten/graphene interface engineering

Irradiation Damage Behavior Research Status of Tungsten-matrix Materials Facing Plasma

Research progress in heat load damage behavior of tungsten and tungsten base materials for nuclear fusion reactor