Abstract:The Mg-Gd-Y-Zn-Zr sheets with different accumulative rolling reduction were successfully prepared through the multi-passes hot rolling process. The accumulative rolling reduction significantly affects the mechanical properties of the resulting sheets through altering the fraction of dynamic recrystallization (DRX) grains and distribution of the broken interdendritic 14H-LPSO phase. In addition, the precipitated equilibrium β phase at grain boundaries can facilitate the DRX process through the particle-stimulated nucleation (PSN) mechanism. The sub-grain boundaries formed in the vicinity of the grain boundaries and within the coarse deformed grains, and then transformed into the high-angle grain boundaries (HAGBs) through incorporating the adjacent dislocation. The coarse deformed grains were also divided into several grains by the formation of HAGBs and the DRX grains at grain boundaries also spread into the coarse deformed grains, and thus the fraction of the DRX grains improved with the increase of the accumulative rolling reduction. The ambient temperature tensile strength anisotropy of the resulting sheets increases with further accumulative rolling reduction. The effectively broken interdendritic 14H-LPSO phases, which acts as the reinforcing short-fiber, significantly strengthen the tensile yield strength along the RD due to its decreased aspect ratio (d/l) and more dispersed distribution aligned along the RD. Thus, the tensile yield strength along the RD demonstrated the higher increment than that along the TD and 45° with increasing accumulative rolling reduction. The broken interdendritic 14H-LPSO phases aligned along the RD also contribute to the higher fracture elongation along the 45° due to its alignment parallel to the resolved maximum shear stress during tension. Furthermore, the larger accumulative strain is conducive to decreasing the tensile anisotropy of the resulting sheets at elevated temperature.

Influences of rolling reduction on sheet metal formability

Evolution of Residual Stress Based on Curvature Coupling in Multi-Roll Levelling

The Influence of Warm Rolling Reduction on Microstructure Evolution, Tensile Deformation Mechanism and Mechanical Properties of an Fe-30Mn-4Si-2Al TRIP/TWIP Steel

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Effects of Accumulative Rolling Reduction on the Microstructure Characteristic and Mechanical Properties of Mg-Gd-Y-Zn-Zr Sheets Processed by Hot Rolling

Effect of rolling reduction on microstructure, texture, mechanical properties and mechanical anisotropy of AZ31 magnesium alloys

Improving Single Pass Reduction During Cold Rolling by Controlling Initial Texture of AZ31 Magnesium Alloy Sheet

Study on Asymmetric Rolling Process Applied to Aluminum Alloy Sheets

Bifurcation Analysis of Forming Limits for an Orthotropic Sheet Metal

Effects of Reduction Partitioning in Two-Stage Cold Rolling on the Surface Ridging Resistance of Ferritic Stainless Steel

Effect of Rolling Parameters on Room-Temperature Stretch Formability of Mg–2Zn–0.5Ca Alloy

Sheet Metal Forming Limit Prediction with Maximum Thickness Reduction Ratio

Enhanced formability of Al–Mg–Si–Zn alloy sheet via dislocation structure and texture during cold rolling

Microstructures and textures in cold-rolled aluminium strip

Influence of Microstructure and Mechanical Properties on Formability in High Strain Rate Rolled AZ31 Magnesium Alloy Sheets

Effect of Rolling Reduction on Microstructure and Mechanical Properties of Mg-9Gd-3Y-0.5Zr Alloys

Microstructure evolution behavior and mechanical mechanisms in a near α-Zr alloy by cold rolling

Characterizing the Shear Deformation during Asymmetric Rolling

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Effects of cold-pre-rolling reduction on precipitation of 2519A aluminum alloy plate

Elucidating the effects of cold rolling route on the mechanical properties of AISI 316L austenitic stainless steel