Abstract:In this work, the hydrogen desorption properties of the novel Mg-Al-H hydrogen storage composites prepared by ball-milling the as-received magnesium hydride (MgH2) and the as-prepared aluminum hydride (AlH3) with different molar ratios (1:1, 1:0.5, and 1:0.25) are investigated systematically. Nonisothermal desorption measurements show that more than 7.51 wt % of hydrogen is released from the Mg-Al-H composites when they are heated from room temperature to 500 degrees C. Thermal analysis by differential scanning calorimeter (DSC) and hydrogen desorption spectrum by mass spectrometer (MS-H-2) are used synchronously to study the desorption process of the Mg-Al-H. The onset hydrogen desorption temperature of MgH2 in the MgH2 + AlH3 composite is dramatically reduced from 320 degrees C for the pure MgH2 to below 252 degrees C. The DSC/MS-H-2 and the X-ray diffraction (XRD) analyses show that the desorption of MgH2 in the Mg-Al-H composite is composed of two steps with the reaction between MgH2 and Al forming Mg17Al12 as the first step and the self-decomposition of the residual MgH2 as the second step. Isothermal desorptions show that the desorption kinetics of the MgH2 in the Mg-Al-H composite is significantly improved. The apparent activation energy for the desorption of MgH2 in the MgH2 + 0.25AlH(3) is reduced to 144.6 kJ/mol, which contributes to the improvement in the desorption kinetics of MgH2. The Johnson-Mehl-Avrami (JMA) kinetic studies indicate that the desorption kinetic model of MgH2 in the Mg-Al-H composite is different from the pure MgH2. Concerning the reversibility, under the conditions of 300 degrees C and 5 MPa H-2, MgH2 in the Mg-Al-H composite is almost fully recovered after absorption for 5 h while it is partially recovered for the pure MgH2. Among the samples studied, the MgH2 + 0.25AlH(3) composite exhibits the highest reversible hydrogen storage capacity of 6.10 wt % (H/M).

Sorption behavior of MgH2-Ti for Hydrogen storage material prepared by high pressure milling

Hydrogen storage properties of the Mg–Ti–H system prepared by high-energy–high-pressure reactive milling

Hydrogen Storage Properties of Nanosized MgH<sub>2</sub>−0.1TiH<sub>2</sub>Prepared by Ultrahigh-Energy−High-Pressure Milling

Magnesium-based hydrogen storage nanomaterials prepared by high energy reactive ball milling in hydrogen at the presence of mixed titanium–iron oxide

High-temperature high-pressure reactive ball milling synthesis of Mg-Ni-based solid-state hydrogen storage materials

Effect of Milling Parameters on the Dehydrogenation Properties of the Mg−Ti−H System

Hydrogen Storage Properties of Mg-doped Ti 1.2 Fe Alloys Synthesized by Mechanical Alloying

Nanoscale Ni as a catalyst in MgH2 for hydrogen storage material

Achieving superior hydrogen storage properties of MgH<sub>2</sub> by the effect of TiFe and carbon nanotubes

Hydrogen Storage Properties of Mg+10% TiFe_(1-x)Cr_x(x=0,0.3) Multi-Phase Alloys

Hydrogen desorption properties of the MgH2-AlH3 composites

Hydriding Characteristics of Mg2NiMg2Ni Prepared by Mechanical Milling of the Product of Hydriding Combustion Synthesis

The Hydrogen Storage Properties and Microstructure of Ti-Doped Sodium Aluminum Hydride Prepared by Ball-Milling

Hydriding Characteristics of Mg2ni Prepared by Mechanical Milling of the Product of Hydriding Combustion Synthesis

Remarkably Improved Hydrogen Storage Properties of Carbon Layers Covered Nanocrystalline Mg with Certain Air Stability

Preparation and hydrogen storage properties of Mg-20 wt.% Mg 2Ni0.8Cr0.2 composite with TiO2 nanoparticles

MgH 2 -Ti/cr（amorphous）composite FOR HYDROGEN STORAGE

Hydrogen Storage Behaviors and Microstructure of MF3 (m=ti, Fe)-doped Magnesium Hydride

Preparation and Hydrogen Storage Properties of Mg-20 Wt.% Mg<sub>2</sub>Ni<sub>0.8</sub>Cr<sub>0.2</sub> Composite with TiO<sub>2</sub> Nanoparticles

Hydrogenation of Nanocrystalline Mg at Room Temperature in the Presence of TiH2

Improvement in the Hydrogen Storage Properties of MgH2 by Adding NaAlH4