Abstract:In this study, ion implantation was used as a surface modification method for active and inactive brazing of alumina ceramics to metals. Alumina was implanted with Ti ions at acceleration voltages of 35kV and 55kV at doses ranging between 2×1017 and 1×1018ions/cm2, with Ni ions at an acceleration voltage of 55kV at doses ranging between 2×1016 and 6×1017ions/cm2, and with Al ions at 55kV with a dose of 2×1017ions/cm2. After implantation, the brazing of alumina to Nb was performed using the active brazing metal Ag70Cu27Ti3 (wt.%) at 850°C/870°C and the inactive brazing metal Ag72Cu28 (wt.%) at 830°C in a vacuum respectively. The surface properties of implanted alumina, e.g., implanted ions depth and concentration distribution, newly formed phases, sheet resistance etc., were studied by Rutherford backscattering (RBS), Glancing X-ray diffraction (GXRD) and four-probe method. Shear strengths of the active and inactive brazing joints were measured. Microstructures of the joints were analyzed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). There is no obvious evidence that Ti and Ni ion implantation can enhance the quality of active brazing joints. However, it has been found that Al ion implantation can significantly increase the shear strengths of active brazing joints to average value 139MPa, which is 30% greater than in non-ion implantation (107MPa). It has also been found that ion implantation can improve the shear strengths of alumina–Nb inactive brazing joints. Maximum average shear strength of the inactive brazing joints can reach 43MPa when Ni ions were used at an acceleration voltage of 55kV in a dose of 2×1017ions/cm2. Finally, the effects of ion implantation on alumina–Nb active and inactive brazing were discussed.

A comparison between ion implantation and laser alloying of pure iron for oxidation resistance improvement

A Study of the Corrosion Resistance of M50NiL Bearing Steel by Ion Implantation

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

The Comparison of the Effects of Nodular Cast Iron Laser Alloying with Selected Substances

Effect of La2o3 on Resistance to High-Temperature Oxidation of Laser Clad Ferrite-Based Alloy Coatings

Influence of Implanted Aluminum Ions on the Oxidation Behavior of M5 Alloy at 500°C

Enhancement of Mechanical Properties and Corrosion Resistance of Cast Iron Alloy Using CO2 Laser Surface Treatment

The effect of silicon on the oxidation behavior of iron aluminide produced using powder metallurgy

Microstructure and high-temperature oxidation resistance of in-situ Al 2 O 3 reinforced AlCrFeTiV high-entropy alloy with boron microalloying

Influence of Aluminum Ions Implanted on Oxidation Behavior of ZIRLO Alloy at 500 °C

Effect of Au-ion irradiation on the morphology, microstructure and lead-bismuth eutectic corrosion behavior of refractory TiNbZrMoV high-entropy alloy coating

Effect of boron on the microstructural evolution and wear resistance of high-hardness Fe-based alloy coatings prepared by laser cladding

Microstructure and corrosion resistance of laser alloying coating in-situ synthesized on ductile iron

On the Efficiency of Laser Alloying of Grey Cast Iron with Tungsten and Silicon Carbides

Characterization of Nano-Oxide Layers Fabricated by Ion Beam Oxidation

High temperature oxidation enhanced by laser remelted of CoCrFeNiAlx (x = 0.1, 0.5 and 1) high-entropy alloys

Microstructural evolution in laser melted boron alloyed Ti-6Al-4V

Effects of ion implantation on the brazing properties of high purity alumina

Oxidation behavior of laser remelted plasma sprayed NiCrAlY and NiCrAlY–Al2O3 coatings

Laser Surface Alloying of Austenitic 316L Steel with Boron and Some Metallic Elements: Properties

Effect of laser remelting on high-temperature oxidation resistance of AlCoCrFeNi high-entropy alloy coating