Abstract:This study investigated the effect of grain size distribution on the deformation behavior in fine-grained (FG) austenitic stainless steels (γ-SSs). Commercial Cr–Mn–N γ-SS was selected as the coarse-grained (CG) specimen, which was cold rolled and then annealed at 1000 °C for 60 s and 700 °C for 3600 s to obtain FG specimens with similar grain sizes but different grain size distributions. The CG specimens annealed at 1000 °C for 60 s and 700 °C for 3600 s were referred to as unimodal-FG and bimodal-FG specimens, respectively. The tensile properties revealed that the yield strength was enhanced from 383 MPa to 685 MPa when the grain size was refined from CG (10.7 μm) to FG (∼1.8 μm). Moreover, the bimodal-FG specimen exhibited a higher total elongation of 48% than 36.5% for the unimodal-FG specimen. Transmission electron microscopy, electron backscatter diffraction and X-ray diffraction were used to identify the microstructural characteristics during tension. The results indicated that the main deformation mechanisms of γ-SSs specimens during tension were dislocation generation and accumulation at the initial stage, deformation twinning at the intermediate stage, and deformation-induced martensite (DIM) at the final stage. Compared with the unimodal-CG counterpart, grain refinement in the unimodal-FG specimens restricted the formation of DIM due to the increased austenite stability. A newly discovered phenomenon was that the bimodal-FG specimens promoted the formation of geometrically necessary dislocation (GND) and DIM compared to the unimodal-FG, which was due to the uneven deformation in grains located on hetero-boundaries (HBs). Moreover, the bimodal-FG specimen was preferentially formed DIM on HBs, especially in the smaller grains side rather than inside larger grains due to the higher stress concentration in smaller grains.

Effect of differences in grain size on the mechanical properties of steel 18Kh2N4MA

Effects of Grain Size on Mechanical Properties and Work‐Hardening Behavior of AISI 304 Austenitic Stainless Steel

Grain Size-Dependent Mechanical Properties of a High-Manganese Austenitic Steel

Effect of Prior Austenite Grain Size on Austenite Reversion, Bainite Transformation and Mechanical Properties of Fe-2Mn-0.2C Steel

Grain Size Dependence of Twinning Behaviors and Resultant Cryogenic Impact Toughness in High Manganese Austenitic Steel

Effect of Grain Refinement on High-Carbon Martensite Transformation and Its Mechanical Properties

The Effects of Prior Austenite Grain Refinement on Strength and Toughness of High-Strength Low-Alloy Steel

The effect of grain size on fracture behaviour in tempered martensite embrittlement for AISI 4340 steel

Grain Size Effect on Fracture Behavior of the Axis-Tensile Test of Inconel 718 Sheet

Effect of Grain Size on the Plastic Deformation Behaviors of a Fe-18Mn-1.3Al-0.6C Austenitic Steel

Effect of grain size on dynamic strain aging behavior of C-bearing high Mn twinning-induced plasticity steel

Effect of Strain Localization on the Mechanical Properties from Nonuniform Grain Size Distribution of Ultralow Carbon Steel

Effects of Initial Austenite Grain Size on Microstructure Evolution of Medium Carbon Steel

EFFECT OF AUSTENITE GRAIN SIZE ON STRAIN ENHANCED TRANSFORMATION IN A LOW CARBON STEEL

Probing the impact of grain size distribution on the deformation behavior in fine-grained austenitic stainless steel: A critical analysis of unimodal structure versus bimodal structure

Effect of grain ultra-refinement on microstructure, tensile property, and corrosion behavior of low alloy steel

The Effects of Grain Size on Ductility of AZ31 Magnesium Alloy

Probing the Impact of Grain Interior and Grain Boundaries on the Mechanical Behavior of a High-Mn Austenitic Steel

Effects of grain size on the precipitation pathway and mechanical properties of (CoCrFeNi)94Ti2Al4 high entropy alloy

A Comparison of Fracture Behavior of Low Alloy Steel with Different Sizes of Carbide Particles

Effect of Prior-Austenite Grain Size on the Microstructure and Mechanical Properties of Ultrafine-Grained Dual-Phase Layer-Structured Steel Produced by Hot Rolling of Intercritical Annealed Bainite