Abstract:The water transport behavior of epoxy coatings on mild steels in sodium chloride (NaCl) solution was studied using the electrochemical impedance spectroscopy (EIS) technique. It was found that, with the increase of the curing agent (polyamide) content, the water diffusion coefficient (D) decreased and then increased, with the minimum at 2.2 molar ratio of epoxy resin to polyamide. The differential scanning calorimetry (DSC) and Fourier transform infrared spectroscopy (FTIR) measurements were used to interpret the variations of D. FTIR tests showed that the chemical structure of epoxy coatings changed with the variation of the curing agent content. It was shown that the lower the polyamide content, the more the free glycidyl groups remained in epoxy paints, leading to the incomplete curing reactions and thereby the larger values of D. When the amount of curing agent was too high, the excess hydrophilic-NH2 group was included in the coatings, resulting in them being more sensitive to water permeation in coatings, and thereby also resulting in the larger values of D. DSC results indicated that the glass transition temperature (T-g) of coatings increased and then decreased with the increase in the curing agent content, with the maximum also at 2.2 molar ratio of epoxy resin to polyamide. The analysis of impedance data of epoxy-coated metal systems was also carried out during the whole immersion period. After intensive immersion, three different kinds of diffusional impedance behavior appeared in EIS spectra at different immersion stages, i.e., Warburg diffusion, the open boundary finite length diffusion, and the blocked finite length diffusion, respectively.

Preparation of double linked waterborne epoxy resin coating using Titanium curing agent and aminopropyltriethoxysilane and its anticorrosive properties

Corrosion Resistance of Waterborne Epoxy Resin Coating Cross-Linked by Modified Tetrabutyl Titanate

Understanding the Role of Silane Pretreatments in an Organic Coating System. Part 1: Corrosion Performance and Interfacial Property

Corrosion resistance of a self-curing waterborne epoxy resin coating

Understanding the Role of Silane Pretreatments in an Organic Coating System. Part 2: a Study of Molecular Dynamics Simulation

Corrosion Resistance of Epoxy Coatings Modified by Bis-Silane Prepolymer on Aluminum Alloy

Preparation and Anticorrosive Performances of Polysiloxane-Modified Epoxy Coatings Based on Polyaminopropylmethylsiloxane-Containing Amine Curing Agent

Fabrication of a nonionic self-emulsifiable waterborne epoxy curing agent with high cure properties

Two-part epoxy-siloxane hybrid corrosion protection coatings for carbon steel

Electrosynthesis of Cerium Containing Silicon Acrylate Coatings with Antifouling and Corrosion Resistant Properties

Preparation and Properties of Waterborne Acrylic-Modified Epoxy Phosphate Resin and Its Coating

Influence of Curing Agent Content on the Performance of Epoxy Coatings on Mild Steels

Preparation of epoxy-based silicone prepolymers with applications in UV-curable coatings

Water uptake of epoxy coatings modified with γ-APS silane monomer

Improving the Corrosion Performance of Epoxy Coatings by Chemical Modification with Silane Monomers

Influence of Epoxy Content on the Properties and Marine Bacterial Adhesion of Epoxy Modified Silicone Coatings

The effect of coupling agents on the anti-corrosion properties of acrylic latex coatings

TEOS-Modified SiC Superhydrophobic Nanostructures in Epoxy Resin Coatings for Corrosion Prevention

Preparation of self-healing water-based epoxy coatings containing microcapsules, treated CeO2 particles and 8HQS corrosion inhibitor, and study of their anti-corrosion properties

Durable and Hydrophobic Self-Healing Coating with Rapid Thermal Activation and Prolonged Corrosion Resistance

A UV-curable silicone acrylate anti-smudge coating containing tertiary amines and Ti with the ability to prevent oxygen inhibition