Abstract:This study investigates the substitution of cerium (Ce) with mischmetal (MM) in cast Al-MM alloys, focusing on microstructure, hardness, tensile and compression properties, creep resistance, and coarsening resistance. Al-MM alloys with various MM compositions (Ce, Ce-50La, Ce-33La, and Ce-27La-19Nd, weight percent) exhibit near-eutectic and hyper-eutectic microstructures for Al-9MM and Al-12MM compositions, respectively, with similar as-cast hardness (~525 MPa). All Al-9MM alloys show tensile yield stress ~55 MPa, ultimate tensile strength ~130 MPa, and fracture strain ~8%.The microstructural and mechanical properties consistency demonstrates the flexibility of MM compositions in Al-MM alloys. Al-9MM exhibits excellent coarsening resistance, with minimal hardness reduction when exposed to 300 and 350 C for up to 11 weeks, and a modest ~15% hardness reduction at 400 C for 8 weeks, outperforming eutectic Al-12.6Si and Al-6.4Ni alloys. Additionally, Al-9MM shows higher creep resistance at 300 C compared to most precipitate-strengthened Al-Sc-Zr and solid-solution-strengthened Al-Mg/Mn alloys, but is outperformed by eutectic-strengthened Al-6.4Ni and Al-10Ce-5Ni alloys.The effect of casting cooling rate is investigated through wedge casting: Al-9Ce transitions from hypo- to hyper-eutectic as cooling rates decrease, while Al-12Ce consistently shows hyper-eutectic microstructures. Al11Ce3 lamellae become finer and more closely spaced with increasing cooling rates. Al-9Ce maintains steady hardness at high to moderate cooling rates but shows reduced hardness at lower rates, whereas Al-12Ce shows no change in hardness.With a 15% reduction in energy consumption and CO2 emissions, Al-Ce alloys where Ce is replaced with MM offer comparable mechanical properties and enhanced environmental benefits, highlighting the potential of MM as a sustainable alternative.

Critical Assessment 40: A search for the eutectic system of high-temperature cast aluminium alloys

Achieving Enhanced Strength Retention at Elevated Temperatures in Ultrafine-Fibrous Interconnected Al-Ce-Ni Eutectic Alloy Solidified under Super-Gravity Field

On the Al-Al11Ce3 Eutectic Transformation in Aluminum-Cerium Binary Alloys

Castable eutectic Ni–Ce high temperature alloys strengthened by γ/γʹ microstructure

Microstructure diversity dominated by the interplay between primary intermetallics and eutectics for Al-Ce heat-resistant alloys

Refining Mechanism and Elevated-Temperature Mechanical Properties of Al-Ce Alloys Solidified under Super Gravity Field

A novel Al-Si-Ni-Fe near-eutectic alloy for elevated temperature applications

Improved High-Temperature Aluminum Alloys Containing Cerium

High-Pressure Die Casting of Al–Ce–La–Ni–Fe Alloys

Evaluation of critical temperatures of as-cast Co-based superalloys as a function of alloying elements and their effect on microstructure

Effects of Mischmetal Composition and Cooling Rates on the Microstructure and Mechanical Properties of Al-(Ce, La, Nd) Eutectic Alloys

Aging Behavior Analysis of Al-Ce-Based Alloys Using Hardness and Microstructural Quantification

Towards Superior High Temperature Properties in Low Density AlCrFeNiTi Compositionally Complex Alloys

A Quantitative Phase Analysis by Neutron Diffraction of Conventional and Advanced Aluminum Alloys Thermally Conditioned for Elevated-Temperature Applications

The roles of solidification cooling rate and (Mn,Cr) alloying elements in the modification of β-AlFeSi and hardness evolvements in near-eutectic Al-Si alloys

Phase equilibria, microstructure, and high temperature oxidation resistance of novel refractory high-entropy alloys

Enhancing ambient and elevated temperature performance of hypoeutectic Al–Ce cast alloys by Al 3 (Sc,Zr) precipitate

Microstructure and solidification behaviour of Ni3Al/Ni7Hf2 eutectic alloy

Step-by-Step Observation of Secondary-Phase Evolution During the Casting Cracking Process in Mg–Ce–Al Alloys

Comparing evolution of precipitates and strength upon aging of cast and laser-remelted Al-8Ce-0.2Sc-0.1Zr (wt.%)