Abstract:A nanometer thick passivation layer will spontaneously form on Li-metal in battery applications due to electrolyte reduction reactions. This passivation layer in rechargeable batteries must have "selective" transport properties: blocking electrons from attacking the electrolytes, while allowing Li+ ion to pass through so the electrochemical reactions can continue. The classical description of the electrochemical reaction, Li+ + e → Li0, occurring at the Li-metal|electrolyte interface is now complicated by the passivation layer and will reply on the coupling of electronic and ionic degrees of freedom in the layer. This passivation layer is called "solid electrolyte interphase (SEI)" and is considered as "the most important but the least understood in rechargeable Li-ion batteries," partly due to the lack of understanding of its structure-property relationship. Predictive modeling, starting from the ab initio level, becomes an important tool to understand the nanoscale processes and materials properties governing the interfacial charge transfer reaction at the Li-metal|SEI|electrolyte interface. Here, we demonstrate pristine Li-metal surfaces indeed dissolve in organic carbonate electrolytes without the SEI layer. Based on joint modeling and experimental results, we point out that the well-known two-layer structure of SEI also exhibits two different Li+ ion transport mechanisms. The SEI has a porous (organic) outer layer permeable to both Li+ and anions (dissolved in electrolyte), and a dense (inorganic) inner layer facilitate only Li+ transport. This two-layer/two-mechanism diffusion model suggests only the dense inorganic layer is effective at protecting Li-metal in electrolytes. This model suggests a strategy to deconvolute the structure-property relationships of the SEI by analyzing an idealized SEI composed of major components, such as Li2CO3, LiF, Li2O, and their mixtures. After sorting out the Li+ ion diffusion carriers and their diffusion pathways, we design methods to accelerate the Li+ ion conductivity by doping and by using heterogonous structure designs. We will predict the electron tunneling barriers and connect them with measurable first cycle irreversible capacity loss. Finally, we note that the SEI not only affects Li+ and e- transport, but it can also impose a potential drop near the Li-metal|SEI interface. Our challenge is to fully describe the electrochemical reactions at the Li-metal|SEI|electrolyte interface. This will be the subject of ongoing efforts.

Capacity losses due to solid electrolyte interphase formation and sodium diffusion in sodium-ion batteries

Fundamental Understanding and Quantification of Capacity Losses Involving the Negative Electrode in Sodium-Ion Batteries

Progressive growth of the solid–electrolyte interphase towards the Si anode interior causes capacity fading

On the Capacity Losses Seen for Optimized Nano‐Si Composite Electrodes in Li‐Metal Half‐Cells

Vulnerable Solid Electrolyte Interphase Deposition in Sodium-Ion Batteries from Insufficient Overpotential Development during Formation

Decoupling First-Cycle Capacity Loss Mechanisms in Sulfide Solid-State Batteries

Effect of Solid Electrolyte Interphase on Sodium-Ion Insertion and Deinsertion in Non-Graphitizable Carbon

Impact of solid-electrolyte interphase reformation on capacity loss in silicon-based lithium-ion batteries

Quantifying capacity loss due to solid-electrolyte-interphase layer formation on silicon negative electrodes in lithium-ion batteries

Solid Electrolyte Interphase Growth and Capacity Loss in Silicon Electrodes

Identifying the Mechanism of Continued Growth of the Solid-Electrolyte Interphase

Modelling the Morphological Background to Capacity Fade in Si-based Lithium-Ion Batteries

Computational Exploration of the Li-Electrode|Electrolyte Interface in the Presence of a Nanometer Thick Solid-Electrolyte Interphase Layer

Investigating the Failure Mechanism of Solid Electrolyte Interphase in Silicon Particles from an Electrochemical-Mechanical Coupling Perspective

Electrolyte Role in SEI Evolution at Si in the Pre-lithiation Stage versus the Post-lithiation Stage

Preformation of Insoluble Solid-Electrolyte Interphase for Highly Reversible Na-Ion Batteries

Insight into the Capacity Fading Mechanism of Amorphous Se2S5 Confined in Micro/Mesoporous Carbon Matrix in Ether-Based Electrolytes.

Transition metal speciation as a degradation mechanism with the formation of a solid-electrolyte interphase (SEI) in Ni-rich transition metal oxide cathodes

Insights on SEI Growth and Properties in Na‐Ion Batteries via Physically Driven Kinetic Monte Carlo Model

(Invited) Initial Capacity Loss Mechanism of All-Solid-State Lithium Sulfide Battery Unraveled By in Situ Neutron Tomography

Capacity Fade due to Side-reactions in Silicon Anodes in Lithium-ion Batteries