Abstract:In this study, the microstructural changes in irradiated W-1 wt%Pr2O3, W-1 wt%La2O3, W-1 wt%TiC and W-1 wt%ZrC specimens by 1 MeV Fe+ ion irradiation to doses of 1 dpa at room temperature have been characterized by transmission electron microscopy (TEM) to understand the radiation damage. The specimens of 1 dpa were consecutively annealed at temperatures of 600 degrees C, 800 degrees C, 900 degrees C and 1100 degrees C for 1h, and the post-irradiation annealing effect on the microstructure was studied. Microstructural features such as dislocations, dislocation loops and dense dislocation networks were observed by the means of TEM. There was a significant change in the microstructure of the tungsten (W) after irradiation and post-irradiation annealing. W-1 wt%TiC likely consisted of fewer radiation-induced defects and hence exhibits higher resistance to radiation-induced microstructural changes than the others. The general trend is that the density of defect clusters decreases while the average size of the clusters increases with the annealing temperature. A complete removal of dislocation structures at 1100 degrees C occurred in all materials. The irradiation damage effect of Fe+ ions on the deuterium retention of as-synthesized W-based composites was investigated. Thermal desorption spectroscopy of W implanted with D-2 (-) ions was performed using the low-energy ion irradiation system of Kyoto University. Compared with the samples without Fe preirradiation, the deuterium retention of the four composites increased after Fe+ pre-irradiation. The retained amount of deuterium was also increased with the increase in the Fe+ irradiation dose. This is of vital importance to the scientific community working on these materials for extreme irradiating environments.

Study of temperature influence on electron beam induced deposition

Substrate temperature and electron fluence effects on metallic films created by electron beam induced deposition

Effect of High Temperature Annealing on the Microstructure and Thermal Shock Resistance of Tungsten Coatings Grown by Chemical Vapor Deposition

Electron beam induced deposition at elevated temperatures: compositional changes and purity improvement

Controlling Electron-Beam-induced Carbon Deposition on Carbon Nanotubes by Joule Heating

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Influence of Nitrogen Pre-Irradiation at Different Temperatures on Surface Blistering and Deuterium Retention in Tungsten

E-beam Induced Carbon Nanowires in TEM

Energy Density Distribution and Temperature Closed-Loop Control in Electron Beam Processing

The Effect of Electron Beam Energy Density on Temperature Field for Electron Beam Melting

Numerical investigation of the impact of thermoelectric effect on electron beam welding of dissimilar materials

Study on Effects of Energy Deposition and Thermal Shock Wave by Electron Beam Irradiation

Measurement of electron beam induced sample heating in SEM experiments

TEM Studies of 1 MeV Fe+ Ion-Irradiated W Alloys by Wet Chemical Method: High-Temperature Annealing and Deuterium Retention

Effects of electron beam heat input mode on microstructure of Ti-6Al-4V

Phase composition of sputter deposited tungsten thin films

Effect of initial exposure temperature on the deuterium retention and surface blistering in tungsten

Thermionic electrons in Electron Beam Powder Bed Fusion process: an Experimental investigation

Transient electrical conductivity of W-based electron beam induced deposits during growth, irradiation and exposure to air

Phase Control and Young's Modulus of Tungsten Thin Film Prepared by Dual Ion Beam Sputtering Deposition

Reflection and implantation of low energy helium with tungsten surfaces