Abstract:Bi2Te3-based materials are dominating thermoelectrics for almost all of the room-temperature applications. To meet the future demands, both their thermoelectric (TE) and mechanical properties need to be further improved, which are the requisite for efficient TE modules applied in areas such as reliable micro-cooling. The conventional zone melting (ZM) and powder metallurgy (PM) methods fall short in preparing Bi2Te3-based alloys, which have both a highly textured structure for high TE properties and a fine-grained microstructure for high mechanical properties. Herein, a mechanical exfoliation combined with spark plasma sintering (ME-SPS) method is developed to prepare Bi0.5Sb1.5Te3 with highly improved mechanical properties (correlated mainly to the dislocation networks), as well as significantly improved thermoelectric properties (correlated mainly to the texture structure). In the method, both the dislocation density and the orientation factor (F) can be tuned by the sintering pressure. At a sintering pressure of 20 MPa, an exceptional F of up to 0.8 is retained, leading to an excellent power factor of 4.8 mW m-1 K-2 that is much higher than that of the PM polycrystalline. Meanwhile, the method can readily induce high-density dislocations (up to ∼1010 cm-2), improving the mechanical properties and reducing the lattice thermal conductivity as compared to the ZM ingot. In the exfoliated and then sintered (20 MPa) sample, the figure-of-merit ZT = 1.2 (at 350 K), which has increased by about ∼20%, and the compressive strength has also increased by ∼20%, compared to those of the ZM ingot, respectively. These results demonstrate that the ME-SPS method is highly effective in preparing high-performance Bi2Te3-based alloys, which are critical for TE modules in commercial applications at near-room temperature.

The Mechanical and Thermoelectric Properties of Bi2Te3-Based Alloy Prepared by Constrained Hot Compression Technique

Ultrasonic-assisted Hot Pressing of Bi2Te3-based Thermoelectric Materials

Improved Thermoelectric Properties of Bi2Te3−xSexalloys by Melt Spinning and Resistance Pressing Sintering

Enhancing the Thermoelectric and Mechanical Properties of Bi 0.5 Sb 1.5 Te 3 Modulated by the Texture and Dense Dislocation Networks

Suppressing the donor-like effect via fast extrusion engineering for high thermoelectric performance of polycrystalline Bi2Te2.79Se0.21

Mid-temperature Thermoelectric Performance of Zone-Melted Sb2(Te,Se)3 Alloys Near Phase Transition Boundary

High Thermoelectric Performance Bismuth Telluride Prepared by Cold Pressing and Annealing Facilitating Large Scale Application

High-performance near-room-temperature n-type Bi2Te3-based thermoelectric alloys with superior mechanical properties

Synergistically Enhanced Thermoelectric and Mechanical Performance of Bi2Te3 Via Industrial Scalable Hot Extrusion Method for Cooling and Power Generation Applications

Simultaneously Improved Thermoelectric and Mechanical Properties Driven by MgB2 Doping in Bi0.4Sb1.6Te3 Based Alloys

Enhanced Thermoelectric and Mechanical Properties of Zone Melted P-Type (bi,sb)2te3 Thermoelectric Materials by Hot Deformation

BiSbTe alloy with high thermoelectric and mechanical performance for power generation

High-Temperature Mechanical and Thermoelectric Properties of p-Type Bi0.5Sb1.5Te3 Commercial Zone Melting Ingots

Gibbs Adsorption and Zener Pinning Enable Mechanically Robust High‐Performance Bi2Te3‐Based Thermoelectric Devices

Melt-Centrifuged (bi,sb)2 Te3 : Engineering Microstructure Toward High Thermoelectric Efficiency.

High-Performance p-Type Bi 2 Te 3 -Based Thermoelectric Materials Enabled via Regulating Bi-Te Ratio

Thermoelectric Properties of Bi2Te3 Alloy Prepared by Mechanical Alloying and Spark Plasma Sintering

Multi-scale hierarchical microstructure modulation towards high room temperature thermoelectric performance in <i>n</i>-type Bi<sub>2</sub>Te<sub>3</sub>-based alloys

Synergistically enhanced thermoelectric and mechanical performance of Bi 2 Te 3 via industrial scalable hot extrusion method for cooling and power generation applications

Enhanced Thermoelectric and Mechanical Performances in Sintered Bi 0.48 Sb 1.52 Te 3 –AgSbSe 2 Composite

Critical Role of Tellurium Self-Compensation in Enhancing the Thermoelectric Performance of P-Type Bi0.4Sb1.6Te3 Alloy