Preparation and Performance Evaluation of La Doped Mn-Co Spinel Coating on Connecting Board of Solid Oxide Electrolysis Cell
WU Jiandi,WANG Qiang,LU Lin,REN Yanlun,YANG Yan,SUN Zhaosong,GUO Tu,WANG Hongtao,ZHANG Li
DOI: https://doi.org/10.16577/j.issn.1001-1560.2023.0265
2023-01-01
Abstract:When metal connecting board of solid oxide electrolysis cell (SOEC) are used for long time in a medium-to-high temperature environment (600~800 ℃), severe surface oxidation increases the internal resistance of the electrolytic cell, and the volatilization of Cr from the metal substrate reduces the electrochemical activity of the electrode. The combined effect of the two leads to severe degradation of the performance of SOEC. In response to the above problems, Mn-Co coating and Mn-Co-La coating were prepared on commercial SUS430 metal substrate by electrophoretic deposition method. Subsequently, with using the process of successively sintering under neutral atmosphere (950 ℃, N2) and oxidizing atmosphere (825 ℃, air) conditions, the strong and dense Mn-Co coatings and Mn-Co-La coatings were obtained. Moreover, the effects of sintering atmosphere and La element doping on coating properties were studied. The morphology, phase composition, element distribution and area specific resistance of the coatings were characterized by scanning electron microscope, X-ray diffractometer, energy spectrometer and four-probe resistivity tester, respectively. Results showed that the coating prepared by electrophoretic co-deposition doping with trace amounts of nano-La2O3 had more uniform and refined grains, which effectively inhibited the overflow of Fe-Cr from the substrate during high-temperature N2 sintering. The results of the 300 h oxidation cycle test at 750 ℃ indicated that compared with the substrate, the sintering process proposed in this work was beneficial to improving the anti-oxidation performance of the coating, and the La-doped coating possessed better performance. Furthermore, the doping of La element effectively slowed down the volatilization of Cr in the substrate, which made the area specific resistance lower and more stable, and improved the high-temperature oxidation resistance of the Mn-Co spinel coating.