Deformation-induced martensite formation and dislocation channeling in neutron-irradiated 316 stainless steel

N. Hashimoto,T.S. Byun
DOI: https://doi.org/10.1016/j.jnucmat.2007.03.204
IF: 3.555
2007-08-01
Journal of Nuclear Materials
Abstract:The deformed microstructure in 316 stainless steel (316SS) after neutron irradiation in the range of 65–100°C to 0.78dpa was investigated by transmission electron microscopy (TEM). Deformation-induced martensite transformation and dislocation channeling were observed at irradiation dose higher than 0.1dpa. Estimation of the resolved shear stress (RSS) associated with each dislocation channel indicated a tendency for the RSS and channel width to be greatest when the angle between tensile axis and slip plane normal is around 45°. Furthermore, channel width increased with increasing RSS, indicating that the most extensive localized channel deformation tends to occur at a high RSS level. Deformation-induced martensite phase was found at various strain levels even at room temperature and tends to be exhibited mainly at intersections of channels. This suggests that a very high stress could lead to the γ→α martensite formation by the spreading of a Shockley partial dislocation over successive 〈111〉fcc planes.
materials science, multidisciplinary,nuclear science & technology
What problem does this paper attempt to address?