Study on microstructure evolution and nanoindentation characteristics of 316 L austenitic stainless steel with inverse gradient grain sizes fabricated via torsion and electro-magnetic induction heating
Jidong Zhang,Weixue Han,Zhenyi Huang,Jinghui Li,Mingya Zhang,Long Zhang
DOI: https://doi.org/10.1016/j.matchar.2021.111462
IF: 4.537
2021-11-01
Materials Characterization
Abstract:An inverse gradient grain size structure (IGSS) was fabricated in 316 L stainless steel by the torsion and subsequent electro-magnetic induction heating (EMIH), where the grain sizes gradually decrease from the surface to the core. The changes in the typical deformation and annealing textures were systematically studied in the torsion samples subjected to EMIH at 750°C and 850°C for different times by electron back scattering diffraction. The results showed that Goss, Brass and cube components are sensitive to temperature, and the content of annealing texture, R and Brass R, increased during EMIH at 850°C, however, the content of deformation textures have small change after EMIH at 750°C and 850°C for 60 s. The density of geometrically necessary dislocations (GNDs) and statistically stored dislocations (SSDs) were investigated by nanoindentation tests, which were performed on the transversal section along the radius. The changes in the density of GNDs and SSDs are similar, both increase first and then decrease from the core to the surface along the radius.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing