Abstract:Deoxidation of Ti, or direct removal of O dissolved in metallic Ti, is known to be extremely difficult when Mg is used as the deoxidizing agent. This difficulty arises because the chemical potential of O 2 , p O2 , under Mg/MgO equilibrium is high (approximately 10 −41 atm at 1200 K) and is equivalent to that of Ti containing ∼2 mass% O at 1200 K. Therefore, when deoxidizing Ti to the commercial level of high-grade pure Ti (below 0.05 mass% O) using an Mg reductant at 1200 K, the activity of the reaction product MgO ( a MgO ) must be decreased to below ∼0.025, which is difficult in practice. In this study, the removal of O in Ti in molten MgCl 2 salt using an electrochemical technique was examined at ∼1173 K with the objective of obtaining Ti containing less than 0.05 mass% O. Ti samples and graphite electrodes immersed in molten MgCl 2 served as the cathode and anode, respectively. A constant voltage was applied between the electrodes using an external DC source. Molten MgCl 2 was employed to produce the deoxidizing agent Mg and to facilitate deoxidation of Ti by decreasing the activity of the reaction product MgO. By applying a voltage of approximately 3.1 V between the electrodes, the chemical potential of Mg in the molten MgCl 2 was increased at the surface of the Ti cathode, and the Ti samples were deoxidized. The resulting O species, mainly formed O 2− dissolved in the molten MgCl 2 , was removed from the molten salt by reacting with the C anode to form CO (or CO 2 ) gas. Ti wires containing 0.12 mass% O were deoxidized to less than 0.02 mass% O. In some cases, the O concentration in the Ti samples was reduced to the level of 0.01 mass%, which cannot be accomplished using the conventional Kroll process. The possible application of this deoxidation technique to practical industrial recycling processes is discussed.

Producing titanium by reducing TiCl2-MgCl2 mixed salt with magnesium in the molten state

Titanium powder production by TiCl4 gas injection into magnesium through molten salts

High-Speed Titanium Production by Magnesiothermic Reduction of Titanium Trichloride

Evolution of Molten Salt Electrolysis in Titanium Production Process

Titanium production by magnesium thermal reduction in the electroslag process

Magnesiothermic Reduction of TiO2 Assisted by LaCl3

Fundamental study on synthesis and enrichment of titanium subchloride

Development of deoxidation process for off-grade titanium sponge using magnesium metal with wire mesh strainer type of crucible

Preparation of Titanium Metal by Deoxygenation Under KCl-NaCl-YCl3 System Using Soluble Anode

Direct oxygen removal technique for recycling titanium using molten MgCl 2 salt

The Kroll process and production of titanium sponge

Effective Deoxidation Process of Titanium Scrap Using MgCl2 Molten Salt Electrolytic

Investigation of the Calciothermic Reduction of TiO 2 for the Green Production of Ti and TiH 2 Powders

Minimizing pest aluminum in magnesium for the production of high-purity titanium

Electrochemical Deoxidation of Titanium and Its Alloy Using Molten Magnesium Chloride

Magnesiothermic Reduction from Titanium Dioxide to Produce Titanium Powder

Carbochlorination of Low-Grade Titanium Slag to Titanium Tetrachloride in Molten Salt

A New Method for Preparing Titanium Aluminium Alloy Powder

Removal of Iron from Titanium Ore through Selective Chlorination Using Magnesium Chloride

Reaction-Mediator-Based Chlorination for the Recycling of Titanium Metal Scrap Utilizing Chloride Waste