Rolling Contact Fatigue and Sliding Wear Performance of Ferritic Nitrocarburized M-50 Steel

J. F. Braza

DOI: https://doi.org/10.1080/10402009208982094

IF: 2.056

1992-01-01

Tribology Transactions

Abstract:The rolling contact fatigue and sliding wear performance of two types of ferritic nitrocarburizing techniques (gaseous and fluidized bed) were evaluated on AISI M-50 steel. These processes produced a thin compound layer over a nitrogen-rich diffusion zone. It was observed that compound layer thicknesses less than 1 μm increased the rolling contact fatigue (RCF) L10 life up to a factor of six over the untreated M-50 steel. Compound layers greater than 2 μm had a tendency to flake off the substrate near the spalled region, producing lower L10 lives than the baseline M-50 steel. Sliding wear tests on ferritic nitrocarburized M-50 showed that the compound layer exhibited slightly larger friction coefficients than the nitrogen-rich diffusion zone, although this layer had slightly greater resistance to catastrophic wear at higher contact stresses. Presented at the 46th Annual Meeting in Montreal, Quebec, Canada April 29–May 2, 1991 Presented at the 46th Annual Meeting in Montreal, Quebec, Canada April 29–May 2, 1991

engineering, mechanical