Abstract:A physically based material model for metals, with elastic–plastic and damage/failure orthotropy is proposed in this paper. The model is defined within the frameworks of irreversible thermodynamics and configurational continuum mechanics and integrated in the isoclinic configuration. The use of the multiplicative decomposition of deformation gradient makes the model applicable to arbitrary plastic and damage deformations. To account for the physical mechanisms of failure, the concept of thermally activated damage initially proposed by Klepaczko (1990) was adopted as the basis for the new damage evolution model. This makes the proposed damage/failure model compatible with the Mechanical Threshold Strength (MTS) model (Follansbee and Kocks, 1988; Chen and Gray, 1996; Goto et al., 2000; Gray et al., 1999; Chen et al., 1998) which was used to control evolution of flow stress during plastic deformation. In addition the constitutive model is coupled with a shock equation of state which allows for modelling of shock wave propagation in the material. The new model was implemented in DYNA3D and our in-house non-linear transient SPH code, MCM (Meshless Continuum Mechanics).Parameters for the new constitutive model for AA7010 (a polycrystalline aluminium alloy, whose orthotropy is a consequence of grain morphology), were derived on the basis of the tensile tests and Taylor anvil tests. The tensile tests were performed for the range of temperatures between 223.15K and 413.15K, and strain rates between 6.4×10-4s-1 and 6.4×101s-1.The new model was validated in two stages. The first stage comprised a series of single element tests design to separately validate elasticity, plasticity and damage related parts of the model. The second stage comprised a series of numerical simulations of Taylor anvil and plate impact tests for AA7010 and comparison of the numerical results with the experimental data. The numerical results illustrate the ability of the new model to predict experimentally observed behaviour.

Problem of long-term high temperature strength of metal materials

Description of step loads at high temperature creep of metallic materials

Experimental and Theoretical Investigations of High-Temperature Creep of the ENAW 5251 (AMg2) Aluminum Alloy under Step Loading

Experimental and theoretical study on high-temperature creep of VT6 titanium alloy under multi-axial loading conditions

Damage Mechanics Considerations for Life Extension of High-Temperature Components

Time-Dependent Deformation and Fracture of Multi-Material Systems at High Temperature

Some Critical Issues in Creep and Fracture Assessment at High Temperature

Some Mechanics Principles for Life Extension of Components at Elevated Temperature

Modeling Of Non-Stationary Creep Processes Under Multiple Loading Conditions By Taking Into Account Damage Accumulation In A Structural Material

Modelling for Creep Cavitation Damage and Life of Three Metallic Materials

Creep-fatigue Damage Level Evaluation Based on the Relationship Between Microstructural Evolution and Mechanical Property Degradation

Hyperelastic effects in brittle materials failure

RECENT PROGRESS IN HIGH TEMPERATURE MECHANICAL BEHAVIOR OF MATERIALS AND STRUCTURES

Modelling of dynamic behaviour of orthotropic metals including damage and failure

Coupling Crystal Plasticity and Continuum Damage Mechanics for Creep Assessment in Cr-based Power-Plant Steel

A Thermodynamically Consistent Creep Constitutive Model Considering Damage Mechanisms

Creep damage and fracture of weldments at high temperature

Refined Deformation Model for Metal-Composite Plates of Regular Layered Structure in Bending Under Conditions of Steady-State Creep

Determining Time-to-Failure in Rocks Using Long-Term Strength Criterion

A new creep damage assessment method for metallic material under variable load conditions at elevated temperature

Theory of the gradual accumulation of fatigue damage in metals under proportional cyclic loading