Abstract:Phenolic resins occupy an important position in industrial applications, but phenol, one of the raw materials for synthesis, is a non-renewable resource. Lignin, as a natural polymer containing phenolic hydroxyl groups, alcohol hydroxyl groups and other reactive groups, can replace some of the phenol in the synthesis of phenolic resins, which can reduce the amount of phenol, thus reducing the cost of phenolic resins, while effectively promoting the high value-added use of renewable biomass resources. Due to its low reactivity, alkaline lignin is usually discharged as production waste, unaware that lignin macromolecules can be modified. In this paper, the phenolic monomers were obtained by acid-catalyzed depolymerization of DES (choline chloride/p-toluenesulfonic acid or choline chloride/lactic acid) from waste alkaline lignin, and the recovery rate of the DES solution during the catalytic treatment was more than 85 %, in which the main monomer was 2-methoxy-4-(1-propyl) phenol. The degradation of alkaline lignin is still favorable after five times of DES solvent recovery. The depolymerized lignin monomer replaced phenol by 50 wt% and then ternary co-polymerized with phenol and formaldehyde to form a biomass phenol-based phenolic resin, providing a green route for phenolic resin production. The cost of resin preparation was economically calculated, and it was found that the cost of resin after accumulating 4 cycles of DES treatment was only 51.1 % of that of pure phenolic resin. The density functional theory (DFT) was used to simulate the possible radical reactions in the intermediate process of phenolic resin reaction, to explore the microscopic mechanism and competition, to provide theoretical reference for further experimental realization of resin structure control and optimization, and to improve the theoretical system of resin synthesis.

The synthesis and characterization of phenolic resin with a high content of dimethylene ether bridges

Novel Silicon-Modified Phenolic Novolac Resins: Non-isothermal Curing Kinetics, and Mechanical and Thermal Properties of Their Biofiber-Reinforced Composites

Synthesis and Characterization of N-phenyl Maleimide Modified Novolac Resin

Silicone-modified Phenolic Resin: Relationships Between Molecular Structure and Curing Behavior

Thermal properties of an epoxy cresol-formaldehyde novolac/diaminodiphenyl sulfone system modified by bismaleimide containing tetramethylbiphenyl and aromatic ether structures

Preparation and Properties of Molybdenum‐modified High‐ortho Thermosetting Phenolic Fiber

Fast Curing Bio-Based Phenolic Resins via Lignin Demethylated under Mild Reaction Condition

Synthesis of a water‐soluble high hydroxymethyl content phenolic resin crosslinker and the associated polyacrylamide weak gel property investigation

Structural Evolution of Phenolic Fibers during the Forming Process

Structure–properties relationship for resols with different formaldehyde/phenol molar ratio

Characterization and properties of phenolic resin doped modified lignin

Synthesis and Characterization of a Liquid Crystalline Epoxy Containing Azomethine Mesogen for Modification of Epoxy Resin

Reactivity and Property of Phenolic Resin Synthesized by Phenol and Paraformaldehyde

Novel Thermosetting Resins Based on 4-(N-maleimidophenyl)glycidylether I. Preparation and Characterization of Monomer and Cured Resins

Preparation of high molecular weight thermoplastic bio-based phenolic resin and fiber based on lignin liquefaction

Preparation and properties of epoxy-modified thermosetting phenolic fiber

Synthesis of Soluble High Molar Mass Poly(Phenylene Methylene)-Based Polymers

Synthesis of phenolic resins by substituting phenol with modified spruce kraft lignin

Synthesis of oligomeric phthalonitrile resins containing imide units and study of the methylene-cyano thermal synergistic polymerization effect

Preparation, Characterization and Thermal Properties of Tetramethylbisphenol F Epoxy Resin and Mixed Systems

Preparation and Microwave Curing of Blended Phenolic Epoxy Fibers