Synthesis of Soluble High Molar Mass Poly(Phenylene Methylene)-Based Polymers

Marco F. D’Elia,Yingying Yu,Melvin Renggli,Madeleine A. Ehweiner,Carina Vidovic,Nadia C. Mösch-Zanetti,Markus Niederberger,Walter Caseri,Marco F. D'Elia

DOI: https://doi.org/10.3390/polym16070967

IF: 5

2024-04-03

Polymers

Abstract:Poly(phenylene methylene) (PPM) is a multifunctional polymer that is also active as an anticorrosion fluorescent coating material. Although this polymer was synthesized already more than 100 years ago, a versatile synthetic route to obtain soluble high molar mass polymers based on PPM has yet to be achieved. In this article, the influence of bifunctional bis-chloromethyl durene (BCMD) as a branching agent in the synthesis of PPM is reported. The progress of the reaction was followed by gel permeation chromatography (GPC) and NMR analysis. PPM-based copolymers with the highest molar mass reported so far for this class of materials (up to Mn of 205,300 g mol−1) were isolated. The versatile approach of using BCMD was confirmed by employing different catalysts. Interestingly, thermal and optical characterization established that the branching process does not affect the thermoplastic behavior and the fluorescence of the material, thus opening up PPM-based compounds with high molar mass for applications.

polymer science

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to develop a general synthetic route for synthesizing poly(phenylene methylene) (abbreviated as PPM) with high molar mass and solubility. Although this multifunctional polymer PPM was synthesized more than 100 years ago, an effective method for preparing PPM materials with high molar mass and good solubility has not been found yet. Specifically, the paper explored the influence of using bifunctional 1,4 - bis(chloromethyl) - 2,3,5,6 - tetramethylbenzene (abbreviated as BCMD) as a branching agent on PPM synthesis and verified it with different catalysts. The research results show that using BCMD can significantly increase the molar mass of PPM, which can be as high as tens of thousands of grams per mole (for example, up to \( \text{M}_n = 205,300 \, \text{g/mol} \)), and this process will not affect the thermoplastic and fluorescent properties of the material. This provides new possibilities for the application of PPM in anti - corrosion coatings, adhesives, aerospace and other fields.